Delamination-resistant heat-shrinkable multilayer oxygen barrier film containing polyester

ABSTRACT

A first multilayer shrink film has an outer polyester layer, an inner 02-barrier layer, and a tie layer between the polyester layer and the barrier layer. A second multilayer film an outer polyester layer, an inner polyamide layer, and a tie layer between the polyester and polyamide layers. The tie layer comprises a styrene-based polymer, and the tie layer in the second film comprises an anhydride functional styrene based copolymer. Included are a packaging article comprising the film, a packaging process utilizing the film, a process for making the film, and a packaged product comprising a packaging article made the film, with a product inside the package.

This application claims priority from provisional U.S. Ser. No.61/976,850, filed 8 Apr. 2014, entitled “Heat-Shrinkable MultilayerBarrier Film Containing High Melt Point Polyester,” which is herebyincorporated, in its entirety, by reference thereto. This applicationalso claims priority from provisional U.S. Ser. No. 61/898,757, filed 1Nov. 2013, also entitled “Heat-Shrinkable Multilayer Barrier FilmContaining High Melt Point Polyester,” which is also herebyincorporated, in its entirety, by reference thereto. This applicationalso claims priority from provisional U.S. Ser. No. 62/055,144, filed 25Sep. 2014, also entitled “Heat-Shrinkable Multilayer Film with Tie LayerBonding Polyester to Polyamide,” which is also hereby incorporated, inits entirety, by reference thereto.

BACKGROUND

Multilayer heat shrinkable films having an oxygen barrier layer havebeen used for the vacuum packaging of oxygen-sensitive products,including food products, and particularly meat products. Upon evacuatingatmosphere from the package followed by sealing the package closed whileunder evacuation, the resulting closed package is thereafter shrunkaround the meat product. Shrinking causes the film to retract againstthe meat product, reducing the amount of excess film protruding awayfrom the meat product, improving the appearance and function of thepackage.

Meat and cheese products, as well as other foods and non-food products,generate abrasion abuse and puncture abuse of the films in which theproducts are packaged. As a result, tough, abrasion-resistant films areneeded for the packaging of various food and non-food products,particularly dense products and/or products with sharp edges, such asbone-in meat products.

Heat shrinkable oxygen barrier films which are shrinkable at relativelylow temperature, have good heat sealability and relatively high strengthhave been developed and used for the packaging of a wide variety ofproducts, including meat products. However, these ethylene-based shrinkfilms were found to lack the abrasion and puncture resistance needed forthe packaging of products which produce high levels of abuse to thepackaging when handled, such as meat and cheese products. As a result,there has been a need for more abuse resistant heat shrinkablemultilayer films having an oxygen barrier layer.

The amount of abuse from abrasion and puncture varies with the productbeing packaged. Some products are highly abusive due to the combinationof the weight and shape of the product as well as any particularly hardand/or sharp portions locations on the product. In recent yearspolyamide-based patchless shrink bags have been commercialized, thesebags providing sufficient abuse resistance for the packaging of meat andcheese products, including some bone-in meat products. However,polyamide-based heat shrinkable films have proven to be unstable duringstorage, shipment, and use. More particularly, polyamide-based filmstend to shrink upon exposure to atmospheric moisture and/or heatencountered during storage and/or transport. This instability isproblematic for subsequent use in packaging meat and other products.

SUMMARY

In an effort to develop a multilayer heat shrinkable oxygen barrier filmhaving improved abuse resistance and temperature stability for thepackaging of meat and cheese products and other food and non-foodoxygen-sensitive products, the inventors of the present inventionconducted research in an effort to develop a suitable packaging filmutilizing a film containing polyester in place of some or all of thepolyamide used in heat shrinkable oxygen barrier films of the prior art.It was discovered that by substituting the polyester for some or all ofthe polyamide, the polyester layers were capable of providing adequatetoughness and abrasion resistance and dimensional stability over time,together with temperature stability superior to correspondingpolyamide-based films.

However, polyester has been found to be difficult to bond to otherthermoplastic film layers for use in a heat shrinkable film. Mostco-extrudable tie layers that have been used to bond to polyester arecomposed of maleic anhydride grafted-ethylene/methylacrylate copolymer(g-EMA). It has been discovered that tie layers made from g-EMA are notsufficient to prevent delamination between the polyester layer and (i)an internal layer comprising polyamide or (ii) an oxygen barrier layermade from ethylene/vinyl alcohol copolymer (EVOH). In such filmsdelamination occurred at the interface between the polyester layer andthe tie layer. The delamination occurred upon shrinking the film, andsometime even during the manufacture of the film.

A solution to the delamination problem was sought in the development ofa tough and abuse-resistant heat shrinkable polyester-containing filmwhich also exhibited the further desired features of: (i) totalunrestrained free shrink at 85° C. of at least 10% using ASTM D 2732,(ii) low oxygen transmission rate, and (iii) heat sealability. It isbelieved that inter-layer shear force is produced during shrinking. Thisshear force may produce delamination if it exceeds the level of adhesionto the adjacent layer.

Investigation revealed that the reason for the delamination duringshrinking was that upon immersion in water at 85° C., the outerpolyester layer was shrinking faster and with greater shrink force thanthe tie layer and additional layers of the film. The less than adequatebonding force between the inner tie layer and the outer polyester layerwas overcome by the differences in the shrink rates of the layers, incombination with the high shrink force of the polyester layer, resultingin delamination.

It has been discovered that the delamination upon shrinking problem canbe overcome by providing the inner tie layer with a styrene-basedpolymer, such as styrene-ethylene-butylene-styrene copolymer. Inmultilayer shrink films having an outer polyester layer and an internaloxygen-barrier layer made from EVOH, with no polyamide between thepolyester layer and the EVOH layer, it was found that delamination couldbe prevented by using a styrene-based polymer that need not containanhydride functionality. However, in films in which the tie layer wasdirectly adhered to both the outer polyester layer and an internalpolyamide layer it was discovered that an anhydride functionalstyrene-based polymer was needed to prevent the film from delaminatingupon shrinking.

Exactly why the styrene-based polymer prevents delamination is notknown. However, factors which could bring about this outcome includeproviding the inner tie layer with greater elasticity, as well asproviding the inner tie layer with a greater bond strength to the outerpolyester layer.

A first aspect is directed to a multilayer heat-shrinkable filmcomprising: (i) a first layer comprising a first polyester, (ii) asecond layer which serves as an O₂-barrier layer, and (iii) a thirdlayer between the first layer and the second layer. The first layer isan outer film layer. The second layer comprises at least one memberselected from the group consisting of saponified ethylene/vinyl acetatecopolymer, polyamide MXD6, polyamide 6I/6T, polyamide 6, polyvinylidenechloride, polyethylene naphthalate, polytrimethylene terephthalate,liquid crystal polymer, and O₂-scavenger. The third layer serves as atie layer and comprises at least one styrene-based copolymer. Themultilayer heat shrinkable film exhibits a total free shrink at 85° C.of at least 10% measured in accordance with a modified free shrink testotherwise in accordance with ASTM D 2732. The polyester is present inthe film in an amount of at least 2 vol %, based on total film volume.

In an embodiment, the third layer (i.e., the tie layer) is directlyadhered to the first layer.

In an embodiment, the film does not have a layer comprising a polyamidebetween the first layer and the second layer.

In an embodiment, the styrene-based polymer makes up from 10 to 100 wt %of the weight of the third layer.

In an embodiment, the third layer comprises the styrene-based polymer inan amount of at least 5 wt %, based on layer weight; or from 5 to 100 wt%, or from 8 to 100 wt %, or from 10 to 100 wt %, or from 10 to 90 wt %,or from 10 to 80 wt %, or from 10 to 60 wt %, or from 10 to 40 wt %, orfrom 10 to 30 wt %, or from 10 to 25 wt %, or from 10 to 20 wt %, orfrom 10 to 15 wt %, or from 50 to 100 wt %, or from 60 to 90 wt %, basedon layer weight.

In an embodiment, the styrene-based polymer comprises at least onemember selected from the group consisting ofstyrene-ethylene-butylene-styrene copolymer, styrene-butadiene-styrenecopolymer, styrene-isoprene-styrene copolymer,styrene-ethylene-butadiene-styrene copolymer,styrene-(ethylene-propylene rubber)-styrene copolymer, andpolystyrene-poly(ethylene-propylene)-polystyrene copolymer.

In an embodiment, the third layer comprises a blend of the styrene-basedcopolymer and at least one member selected from cyclic olefin copolymerand ethylene/unsaturated ester copolymer.

In an embodiment, the third layer comprises a blend of the styrene-basedpolymer and an acrylate based polymer. In an embodiment, thestyrene-based polymer makes up from 5 to 95 wt % of the blend, and theacrylate based polymer makes up from 5 to 95 wt % of the blend, and thestyrene-based polymer and the acrylate based together make up at least70 wt % of the blend.

In an embodiment, the styrene-based polymer makes up from 5 to 40 wt %of the blend, and the acrylate based polymer makes up from 60 to 95 wt %of the blend.

In an embodiment, the styrene-based polymer makes up from 10 to 20 wt %of the blend, and the acrylate based polymer makes up from 80 to 90 wt %of the blend.

In an embodiment in which the third layer comprises a blend of thestyrene-based polymer and a cyclic polymer, the styrene-based polymercan make from 5 to 95 wt % of the blend, and the cyclic polymer makes upfrom 5 to 95 wt % of the blend, with the styrene-based polymer and thecyclic polymer together making up at least 70 wt % of the blend. In anembodiment, the styrene-based polymer makes up from 60 to 95 wt % of theblend, and the cyclic polymer makes up from 5 to 40 wt % of the blend.In an embodiment, the styrene-based polymer makes up from 80 to 90 wt %of the blend, and the cyclic polymer makes up from 10 to 20 wt % of theblend.

In an embodiment, the third layer comprises a blend of the styrene-basedpolymer and a modified polyolefin. In an embodiment, the styrene-basedpolymer makes up from 5 to 95 wt % of the blend, and the modifiedpolyolefin makes up from 5 to 95 wt % of the blend, and thestyrene-based polymer and the modified polyolefin together make up atleast 70 wt % of the blend. In an embodiment, the styrene-based polymermakes up from 5 to 40 wt % of the blend, and the modified polyolefinmakes up from 60 to 95 wt % of the blend. In an embodiment, thestyrene-based polymer makes up from 10 to 20 wt % of the blend, and themodified polyolefin makes up from 80 to 90 wt % of the blend.

In an embodiment, the third layer comprises a blend of the styrene-basedpolymer, an acrylate based polymer, and a cyclic polymer. In anembodiment, the styrene-based polymer makes up from 5 to 90 wt % of theblend, the acrylate based polymer makes up from 5 to 90 wt % of theblend, and the cyclic polymer makes up from 5 to 90 wt % of the blend,and the styrene-based polymer, the acrylate based polymer, and thecyclic polymer together make up at least 70 wt % of the blend. Thestyrene-based polymer makes up from 5 to 40 wt % of the blend, theacrylate based polymer makes up from 20 to 90 wt % of the blend, and thecyclic polymer makes up from 5 to 40 wt % of the blend. Thestyrene-based polymer makes up from 10 to 20 wt % of the blend, theacrylate based polymer makes up from 30 to 80 wt % of the blend, and thecyclic polymer makes up from 10 to 20 wt % of the blend.

In an embodiment, the third layer comprises a blend of the styrene-basedpolymer, an acrylate based polymer, and a modified polyolefin. In anembodiment, the styrene-based polymer makes up from 5 to 90 wt % of theblend, the acrylate-based polymer makes up from 5 to 90 wt % of theblend, and the modified polyolefin makes up from 5 to 90 wt % of theblend, and the styrene-based polymer, the acrylate-based polymer, andthe modified polyolefin together make up at least 70 wt % of the blend.The styrene-based polymer makes up from 5 to 40 wt % of the blend, theacrylate-based polymer makes up from 20 to 90 wt % of the blend, and themodified polyolefin makes up from 5 to 40 wt % of the blend. Thestyrene-based polymer makes up from 10 to 20 wt % of the blend, theacrylate-based polymer makes up from 30 to 80 wt % of the blend, and themodified polyolefin makes up from 10 to 20 wt % of the blend.

In an embodiment, the inner third layer comprises a blend of thestyrene-based polymer, a cyclic polymer, and a modified olefincopolymer. In an embodiment, the styrene-based polymer makes up from 5to 90 wt % of the blend, the cyclic polymer, makes up from 5 to 90 wt %of the blend, and the modified olefin copolymer makes up from 5 to 90 wt% of the blend, and the styrene-based polymer, the cyclic polymer, andthe modified polyolefin together make up at least 70 wt % of the blend.The styrene-based polymer makes up from 5 to 40 wt % of the blend, thecyclic polymer can makes up from 20 to 90 wt % of the blend, and themodified olefin copolymer makes up from 5 to 40 wt % of the blend. Thestyrene-based polymer makes up from 10 to 20 wt % of the blend, thecyclic polymer makes up from 30 to 80 wt % of the blend, and themodified olefin copolymer makes up from 10 to 20 wt % of the blend.

In an embodiment, the inner third layer comprises a blend of thestyrene-based polymer, an acrylate based polymer, a cyclic polymer, anda modified polyolefin. In an embodiment, the styrene-based polymer makesup from 5 to 85 wt % of the blend, the acrylate-based polymer makes upfrom 5 to 85 wt % of the blend, the cyclic polymer makes up from 5 to 85wt % of the blend, and the modified polyolefin makes up from 5 to 85 wt% of the blend, with the styrene-based polymer, the acrylate-basedpolymer, the cyclic polymer and the modified polyolefin together makingup at least 70 wt % of the blend. In an embodiment, the styrene-basedpolymer makes up from 10 to 40 wt % of the blend, the acrylate-basedpolymer makes up from 10 to 40 wt % of the blend, the cyclic polymermakes up from 10 to 40 wt % of the blend, and the modified polyolefinmakes up from 10 to 40 wt % of the blend. In an embodiment, thestyrene-based polymer makes up from 10 to 20 wt % of the blend, theacrylate-based polymer makes up from 10 to 80 wt % of the blend, thecyclic polymer makes up from 5 to 20 wt % of the blend, and the modifiedpolyolefin makes up from 10 to 80 wt % of the blend.

In an embodiment, the cyclic olefin copolymer comprisesethylene/norbornene copolymer.

In an embodiment, the blend further comprises at least one memberselected from the group consisting of a second polyester and a modifiedpolyolefin.

In an embodiment, the second polyester comprises a copolyester, and theblend comprises: (i) at least one member selected from the groupconsisting of styrene-ethylene-butylene-styrene block copolymer andstyrene-butadiene block copolymer, (ii) ethylene/acrylate copolymer; and(iii) at least one member selected from the group consisting ofcopolyester and anhydride-modified polyolefin.

In an embodiment, the blend comprises: (i) from 10 to 90 wt %, based ontotal blend weight, of at least one member selected from the groupconsisting of styrene-ethylene-butylene-styrene triblock copolymer andstyrene-butadiene multiblock copolymer; (ii) ethylene/methyl acrylatecopolymer in an amount of from 10 to 90 wt %, based on total blendweight; and (iii) from 5 to 30 wt %, based on total blend weight, of atleast one member selected from the group consisting of amorphouscopolyester having a melting point of from 100° C. to 185° C., andanhydride-modified ethylene/alpha-olefin copolymer.

In an embodiment, the copolyester is a semi-crystalline, thermoplastic,linear saturated copolyester having a density of from 1.15 to 1.30g/cm³, a melting point of from 115° C. to 125° C., and a melt index offrom 0.5 to 2 g/10 min.

In an embodiment, the blend comprises from 5 to 15 wt %, based on totalblend weight, of at least one member selected from the group consistingof copolyester having a melting point of from 105° C. to 140° C. andanhydride-modified linear low density polyethylene.

In an embodiment in which the tie layer comprises a modified polyolefin,the modified polyolefin can comprise at least one member selected fromthe group consisting of a grafted anhydride functionality, acopolymerized anhydride functionality, and a blend of the polyolefin andanother polymer having an anhydride functionality.

In an embodiment in which the tie layer comprises an acrylate-basedpolymer, the acrylate based polymer can comprise at least one memberselected from the group consisting of ethylene/methyl acrylatecopolymer, ethylene/ethyl acrylate copolymer, ethylene/butyl acrylatecopolymer, and ethylene/vinyl acetate copolymer.

In an embodiment in which the tie layer comprises a cyclic polymer, thecyclic polymer can comprise at least one member selected from the groupconsisting of ethylene/norbornene copolymer, andethylene/tetracyclododecene copolymer, and cyclic olefin polymer.

In an embodiment, the second layer comprises saponified ethylene vinylacetate copolymer.

In an embodiment, the first polyester comprises at least onesemi-crystalline polyester selected from the group consisting ofpolyethylene terephthalate homopolymer, polyethylene terephthalatecopolymer, polybutylene terephthalate homopolymer, polybutyleneterephthalate copolymer, polynaphthalene terephthalate homopolymer,polynaphthalene terephthalate copolymer, polyethylene furanoatehomopolymer, and polyethylene furanoate copolymer, wherein thesemicrystalline polyester has a melting point of from 80° C. to 265° C.

In an embodiment, the first polyester comprises polyethyleneterephthalate homopolymer having a melting point of at least 240° C.

In an embodiment, the polyethylene terephthalate homopolymer has amelting point of at least 240° C. and is present in the first layer inan amount of at least 95 wt %, based on the weight of the first layer.

In an embodiment, the first polyester comprises amorphous polyester.

In an embodiment, the polyester has a melting point of at least 240° C.and is present in the film in an amount making up at least 25 volume %of the film and comprises at least one member selected from the groupconsisting of polyethylene terephthalate and polyethylene furanoate.

In an embodiment, at least 50 wt % of polyester in the film is presentin the outer film layer, based on total polyester in the film, or atleast 60 wt % of the polyester is present in the outer film layer, or atleast 70 wt % of the polyester is present in the outer film layer, or atleast 80 wt % of the polyester is present in the outer film layer, or atleast 90 wt % of the polyester is present in the outer film layer, or atleast 95 wt % of the polyester is present in the outer film layer, or100 wt % of the polyester is present in the outer film layer, based ontotal polyester in the film.

In an embodiment, the film does not have an internal layer comprisingpolyester. In an embodiment, the polyester is a copolyester.

In an embodiment, the film has an internal layer comprising polyesterand the polyester is in an interpenetrating polymer network. In analternative embodiment, the film has an internal layer comprisingpolyester but the polyester which is not in an interpenetrating polymernetwork.

In an embodiment, the multilayer heat-shrinkable film has a thickness offrom 0.7 mil to 10 mils, or from 1 mil to 8 mils, or from 1.1 mil to 7mils, or from 1.2 mil to 6 mils, or from 1.2 mils to 5 mils, or from 1.3to 4 mils, or from 1.4 to 3.5 mils, or from 1.3 to 1.7 mils, or from 2to 4 mils, or from 2.5 to 3 mils, or from 1.2 to 4 mils.

In an embodiment, the polyester having a melt point of at least 240° C.makes up from 25 to 80 volume % of the film, or from 25 to 70 volume %of the film, or from 25 to 60 volume % of the film, or from 25 to 50volume % of the film, or from 27 to 49 volume % of the film, or from 28to 47 volume % of the film, or from 29 to 46 volume % of the film.

In an embodiment, the multilayer heat shrinkable film has a total freeshrink at 85° C. of from 10% to 130%, measured in accordance with amodified free shrink test otherwise in accordance with ASTM D 2732, or atotal free shrink at 85° C. of from 20% to 100%, or a total free shrinkat 85° C. of from 70% to 110%, or a total free shrink at 85° C. of from30% to 90%, or a total free shrink at 85° C. of from 40% to 80%, or atotal free shrink of at least 15% at 85° C., or a total free shrink ofat least 20% at 85° C., or a total free shrink of at least 30% at 85°C., or a total free shrink of at least 40% at 85° C., or a total freeshrink of at least 50% at 85° C.

In an embodiment, the multilayer film does not exhibit visibledelamination upon undergoing unrestrained free shrink upon immersion inwater at 85° C. for 8 seconds, using ASTM D 2736.

In an embodiment, the film exhibits a total free shrink at 85° C. of atleast 30% measured in accordance with the modified free shrink testotherwise in accordance with ASTM D 2732, and the first polyester ispresent in the film in an amount of at least 15 vol %, based on totalfilm volume.

In an embodiment, the multilayer, heat-shrinkable film exhibits a totalfree shrink at 85° C. of from 40% to 90% measured in accordance with themodified free shrink test otherwise in accordance with ASTM D 2732, andthe first polyester is present in the film in an amount of at least 20vol %, based on total film volume.

In an embodiment, the multilayer film exhibits a shrink stress of atleast 3.1 MPa measured in accordance with ASTM D2838-09, or at least 3.5MPa, or at least 4 MPa, or at least 5 MPa, measured in accordance withASTM D2838-09.

In an embodiment, the multilayer, heat-shrinkable film further comprisesa fourth layer which is a second outer layer and which serves as a heatseal layer and which comprises at least one member selected from thegroup consisting of polyolefin, polyamide, polyester, polyvinylchloride, and ionomer resin.

In an embodiment, the heat seal layer comprises at least one memberselected from the group consisting of, polyolefin, polyamide 6/12,polyamide 12, ionomer resin, ethylene unsaturated acid copolymer,ethylene/unsaturated ester copolymer, polyester having melting point ofup to 150° C., homogeneous ethylene/alpha-olefin copolymer,heterogeneous ethylene/alpha-olefin copolymer, ethylene homopolymer,ethylene/vinyl acetate copolymer, and ionomer resin.

In an embodiment, the heat seal layer makes up from 5 to 40 volumepercent, based on total film volume, or from 10 to 30 volume percent, orfrom 15 to 25 volume percent, or from 10 to 60 volume percent, based ontotal film volume, or from 15 to 55 volume percent, or from 17 to 50volume percent, or from 19 to 46 volume percent, based on total filmvolume.

In an embodiment, the heat seal layer further comprises a slip agent andan antiblock agent.

In an embodiment, the heat seal layer comprises a blend of a homogeneousethylene/alpha-olefin copolymer (e.g., having a density of from 0.89 to0.91 g/cm³) and a heterogeneous ethylene/alpha-olefin copolymer (e.g.,LLDPE).

In an embodiment, the heat seal layer comprises a blend of from 75 to 90wt % homogeneous ethylene/alpha-olefin copolymer having a density offrom 0.895 to 0.905 g/cm³, and from 10 to 25 wt % of a heterogeneousethylene/alpha-olefin copolymer having a density of from 0.915 to 0.925g/cm³.

In an embodiment, the third layer is a first third layer and themultilayer heat-shrinkable film further comprises a fifth layer which isbetween the fourth layer and the second layer, the fifth layer servingas a second tie layer, the fifth layer comprising at least one memberselected from the group consisting of modified polyolefin, modifiedethylene/unsaturated acid copolymer, modified ethylene/unsaturated estercopolymer, and polyurethane. In an embodiment, the second tie layer cancomprise an anhydride modified linear low density polyethylene.

In an embodiment, the second tie layer comprises a blend of from 50 to85 wt % of a modified ethylene/alpha-olefin copolymer with from 50 to 15wt % of modified ethylene/vinyl acetate copolymer having a vinyl acetatecontent of from 6 to 15 wt %.

In an embodiment, the multilayer heat shrinkable film further comprisesa sixth layer which is between the second layer and the fifth layer, thesixth layer comprising at least one member selected from the groupconsisting of (i) an amorphous polyamide, (ii) a blend of asemicrystalline polyamide and amorphous polyamide, and (iii) a blend ofpolyamide 6/12 and a different semi-crystalline polyamide. The sixthlayer provides the multilayer heat shrinkable film with additionalimpact strength and toughness.

In an embodiment, the sixth layer comprises a blend of amorphouspolyamide and polyamide 6, or a blend of amorphous polyamide andpolyamide 6/66.

In an embodiment, the sixth layer comprises a blend of (i) from 60 to 95wt % of at least one member selected from the group consisting ofpolyamide 6 and polyamide 6/66, and (ii) from 5 to 40 wt % of polyamide6I/6T.

In an embodiment, the sixth layer makes up from 1 to 40 percent of thetotal film thickness, or from 3 to 20 percent of the total filmthickness, or from 3-10 percent of the total film thickness, or from 4to 6 percent of the total film thickness.

In an embodiment, the sixth layer comprises a blend of polyamide 6/66 orpolyamide 6 and polyamide 6I/6T. The blend can comprise from 50 to 95 wt% polyamide 6/66 or polyamide 6 and from 5 to 50 wt % polyamide 6I/6T,or from 60 to 95 wt % polyamide 6/66 or polyamide 6 and from 5 to 40 wtpolyamide 6I/6T, or from 70 to 95 wt % polyamide 6/66 or polyamide 6 andfrom 5 to 30 wt % polyamide 6I/6T, or from 80 to 95 wt % polyamide 6/66or polyamide 6 and from 5 to 20 wt % polyamide 6I/6T, or from 85 to 95wt % polyamide 6/66 or polyamide 6 and from 5 to 15 wt % polyamide6I/6T.

In an embodiment, film contains polyamide in an amount less than 10weight percent, based on total film weight, based on total film weight,or in an amount less than 9 weight percent, or in an amount less than 8weight percent, or in an amount less than 7 weight percent, or in anamount less than 6 weight percent, or in an amount from 1 to 6 weightpercent, based on total film weight.

In an embodiment, film does not contain polyamide.

In an embodiment, the film does not comprise an internal layercomprising polyamide.

In an embodiment, the film does not comprise an outer layer comprisingpolyamide.

In an embodiment, the third layer is the only layer in the filmcomprising a styrene based polymer.

In an embodiment, the film has only one layer comprising a styrene-basedpolymer.

In an embodiment, the multilayer heat shrinkable film further comprisesa supplemental tie layer between the second layer and the third layer,with the supplemental tie layer comprising at least one member selectedfrom the group consisting of modified polyolefin, modified acidcopolymer, modified ester copolymer, and polyurethane.

In an embodiment, the supplemental tie layer comprises a blend of from50 to 85 wt % of a modified ethylene/alpha-olefin copolymer with from 50to 15 wt % of modified ethylene/vinyl acetate copolymer having a vinylacetate content of from 6 to 15 wt %, In an embodiment, the supplementaltie layer is directly adhered to the third layer and directly adhered tothe second layer.

In an embodiment, the supplemental tie layer comprises at least onemember selected from the group consisting of modifiedethylene/alpha-olefin copolymer, modified ethylene/unsaturated estercopolymer, and modified ethylene/unsaturated acid copolymer.

In an embodiment, the modified polyolefin comprises anhydride modifiedlinear low density polyethylene. The anhydride modified linear lowdensity polyethylene can make up at least 80 weight % of thesupplemental tie layer, or at least 90 weight % of the supplemental tielayer, or at least 95 weight % of the supplemental tie layer, or 100weight % of the supplemental tie layer.

In an embodiment, the multilayer heat shrinkable film is a seamlesstubing having a lay-flat width of from 40 to 1000 millimeters, athickness of from 1 to 2 mils, and a total free shrink at 85° C. of from40% to 90% measured in accordance with a modified free shrink testotherwise in accordance with ASTM D 2732.

In an embodiment, the multilayer heat shrinkable film is a seamlesstubing having a lay-flat width of from 300 to 1000 millimeters, athickness of from 2 to 5 mils, and a total free shrink at 85° C. of from40% to 90% measured in accordance with a modified free shrink testotherwise in accordance with ASTM D 2732.

A second aspect is directed to a packaging article comprising amultilayer heat shrinkable film heat sealed to itself. The multilayerfilm is in accordance with the first aspect, described above, as well asany and all combinations of non-conflicting embodiments of the firstaspect, described above. The packaging article is a member selected fromthe group consisting of end-seal bag, side-seal bag, L-seal bag,backseamed bag, and pouch.

A third aspect is directed to a packaging process comprising: (a)providing a strand of a flat, heat-shrinkable, multilayer film inaccordance with the first aspect, described above (as well as any andall combinations of non-conflicting embodiments of the first aspect,described above), (b) utilizing the film in a flow wrap process toproduce a partially packaged product comprising a backseamed packagingarticle having a bottom seal and an open top, the packaging articlehaving a product therein, (c) evacuating atmosphere from within thepackaging article and sealing the open top of the packaging articleclosed so that the product is surrounded by the packaging article, and(d) shrinking the packaging article around the product.

In an embodiment, the process is carried out intermittently, and thepackaging article has a first portion of the backseam made beforeprocess interruption and a second portion of the backseam made afterprocess interruption, and the packaging article has a burst strength ashigh as the burst strength of a corresponding package in which theentire backseam was continuously produced without interruption.

In an embodiment, the process is carried out intermittently, and thepackaging article has a first portion of the backseam made beforeprocess interruption and a second portion of the backseam made afterprocess interruption, and the packaging article has a burst strength atleast 95 percent as high as the burst strength of a correspondingpackage in which the entire backseam was continuously produced withoutinterruption, or at least 90 percent as high, or at least 85 percent ashigh, or at least 80 percent as high, or at least 75 percent as high, orat least 70 percent as high, as the burst strength of a correspondingpackage in which the entire backseam was continuously produced withoutinterruption.

A fourth aspect is directed to a process for making a heat-shrinkableannular film, comprising: (I) coextruding an annular multilayerextrudate downward from an annular die, (II) quenching the annularextrudate by applying a quenching liquid to the annular extrudate, (III)reheating the extrudate to an orientation temperature of from 54° C. to99° C., resulting in a reheated annular extrudate, and (IV) orientingthe reheated annular extrudate while the reheated annular extrudate isin the solid state, the orientation being carried out with a totalorientation factor of at least 2, so that an oriented, multilayer,heat-shrinkable film is produced. The coextruded annular extrudatecomprises: (a) a first layer comprising a first polyester, the firstlayer being an outer layer, (b) a second layer which serves as anO₂-barrier layer, the second layer comprising at least one memberselected from the group consisting of saponified ethylene/vinyl acetatecopolymer, polyamide MXD6, polyamide 6I/6T, polyamide 6, polyvinylidenechloride, polyethylene naphthalate, polytrimethylene terephthalate,liquid crystal polymer, and O₂-scavenger, and (c) a third layer betweenthe first layer and the second layer, the third layer serving as a tielayer, the third layer comprising at least one styrene-based copolymer.The orientation is carried out so that the oriented, multilayerheat-shrinkable film exhibits a total free shrink at 85° C. of at least10 percent measured in accordance with a modified free shrink testotherwise in accordance with ASTM D 2732, and the first polyester ispresent in the film in an amount of at least 2 volume %, based on totalfilm volume. The process can be carried out so that the oriented,multilayer heat-shrinkable film is in accordance with the first aspect,described above, including any and all combinations of non-conflictingembodiments of the first aspect, described above.

In an embodiment, the quenching liquid absorbs heat from the annularextrudate as at least 50% of the quenching liquid cascades down theannular extrudate for a distance of at least 2 inches, and quenchingliquid making initial contact with the annular extrudate at a distanceof from 0.1 to 8 inches downstream of a point at which the annularextrudate emerges from the annular die. This process can be carried outas illustrated in FIG. 15, described below.

Alternatively, the process can be carried out as illustrated anddescribed in U.S. Pat. No. 7,744,806, to Broadus et al, entitled“Process for Making Shrink Film Comprising Rapidly-QuenchedSemi-Crystalline Polyamide,” which is hereby incorporated, in itsentirety, by reference thereto. See particularly the apparatusillustrated in FIGS. 2A, 2C, 3, and 4 thereof, and portions ofspecification describing same.

In an embodiment, the process further comprises annealing the multilayerheat-shrinkable film after it has been oriented in the solid state.

In an embodiment, all layers of the multilayer are simultaneouslycoextruded.

A fifth aspect is directed to a packaged product comprising a packagingarticle made from a multilayer heat shrinkable film and a productcomprising food inside the package. The multilayer heat shrinkable filmis in accordance with the first aspect, described above, including anyand all combinations of non-conflicting embodiments of the first aspectdescribed above.

A sixth aspect is directed to a multilayer heat-shrinkable film having(A) a first outer layer containing polyester, (B) a second outer layerwhich serves as a heat seal layer, (C) a first inner layer comprising apolyamide, and (D) a second inner layer which is between the first innerlayer and the first outer layer and which serves as a tie layer to bondthe first outer layer to the inner polyamide layer. The second innerlayer comprises a blend of: (i) a first blend component comprising ananhydride-functional polyolefin; (ii) a second blend componentcomprising at least one member selected from the group consisting ofstyrene/maleic anhydride copolymer, anhydride-functionalstyrene-ethylene-butylene-styrene copolymer, anhydride-functionalstyrene-butadiene-styrene copolymer, anhydride functionalstyrene-isoprene-styrene copolymer, anhydride-functionalstyrene-ethylene-butadiene-styrene copolymer, and anhydride-functionalgrafted styrene-(ethylene-propylene rubber)-styrene copolymer; and (iii)a third blend component comprising a second polyester. The multilayerheat-shrinkable film exhibits a total free shrink at 85° C. of at least10 percent measured in accordance with a modified free shrink testotherwise in accordance with ASTM D 2732. The first polyester is presentin the film in an amount of at least 5 volume %, based on total filmvolume.

In an embodiment, the first inner layer comprises at least one memberselected from the group consisting of: (a) a blend of a semi-crystallinepolyamide and an amorphous polyamide; (b) a blend of a semi-crystallinepolyamide and polyamide 6/12; and (c) 100% amorphous polyamide.

In an embodiment, the first blend component comprises ananhydride-functional ethylene/alpha-olefin copolymer, and the secondblend component comprises anhydride-functional styrene/butadiene blockcopolymer.

In an embodiment, the third blend component comprises asemi-crystalline, thermoplastic, linear saturated polyester resin havinga density of from 1.15 to 1.30 g/cm³, a melting point of from 150° C. to160° C., and a melt index of from 0.5 to 2 g/10 min.

In an embodiment, the first outer layer makes up from 5 to 20 volume %based on total film volume, the second outer layer makes up from 15 to40 volume % based on total film volume, the first inner layer makes upfrom 10 to 30 volume % based on total film volume, and the second innerlayer makes up from 10 to 30 volume % based on total film volume.

In an embodiment, the film has a total thickness of from 1.5 mils to 4mils, or from 2 to 3.5 mils, or from 2.5 to 3 mils.

In an embodiment, the first blend component makes up from 30 to 80 wt %based on total layer weight, the second blend component makes up from 10to 50 wt % based on total layer weight, and the third blend componentmakes up from 2 to 20 wt % based on total layer weight.

In an embodiment, the first blend component makes up from 40 to 70 wt %based on total layer weight, the second blend component makes up from 20to 40 wt % based on total layer weight, and the third blend componentmakes up from 5 to 15 wt % based on total layer weight.

In an embodiment, the first polyester comprises polyethyleneterephthalate having a melting point of at least 240° C.

In an embodiment, the second inner layer is directly adhered to both thefirst outer layer and the first inner layer.

In an embodiment, the film exhibits a total free shrink at 85° C. of atleast 20 percent measured in accordance with a modified free shrink test(disclosed below) otherwise in accordance with ASTM D 2732; or at least30 percent, or at least 40 percent, or at least 50 percent, or at least55 percent, or at least 60 percent, in accordance with the modified freeshrink test otherwise in accordance with ASTM D 2732.

In an embodiment, the second outer layer which serves as the heat seallayer comprises at least one member selected from the group consistingof polyolefin, polyamide 6/12, polyamide 12, ionomer resin,ethylene/unsaturated acid copolymer, ethylene/unsaturated estercopolymer, and polyester having melting point of up to 150° C.

In an embodiment, the heat seal layer further comprises a slip agent andan antiblock agent.

In an embodiment, the second outer layer comprises a homogeneousethylene/alpha-olefin copolymer having a density of from 0.89 to 0.91g/cm³.

In an embodiment, the film further comprises (E) a third inner layerwhich serves as an O₂-barrier layer, the third inner layer comprising atleast one member selected from the group consisting of saponifiedethylene/vinyl acetate copolymer, polyamide MXD6, polyamide 6I/6T,polyamide 6, polyvinylidene chloride, polyethylene naphthalate,polytrimethylene terephthalate, liquid crystal polymer, andO₂-scavenger. The third inner layer is between the first inner layer andthe second outer layer.

In an embodiment, the film further comprises (F) a fourth inner layerwhich serves as a second tie layer, the fourth inner layer being betweenthe second outer layer and the third inner layer, and (G) a fifth innerlayer between the third inner layer and the fourth inner layer, thefifth inner layer comprising a blend of at least one member selectedfrom the group consisting of: (a) a blend of a semi-crystallinepolyamide and an amorphous polyamide, (b) a blend of a semi-crystallinepolyamide and polyamide 6/12, and (c) 100% amorphous polyamide.

In an embodiment, the first inner layer and the fifth inner layer havethe same composition. In another embodiment, the first inner layer andthe fifth inner layer have different compositions.

In an embodiment, the first inner layer and the fifth inner layer havethe same thickness. In another embodiment, the first inner layer and thefifth inner layer have different.

In an embodiment the first inner layer and the fifth inner layer havethe same composition and are the same thickness.

In an embodiment, the third inner layer, which is an O₂-barrier layer,is directly adhered to both the first inner layer and the fifth innerlayer.

In an embodiment, the polyester in the first outer layer comprisespolyethylene terephthalate copolymer in an amount of at least 95 wt %,based on total layer weight. In combination therewith, the second outerlayer may comprise a blend of from 75 to 90 wt % homogeneousethylene/alpha-olefin copolymer having a density of from 0.895 to 0.905g/cm³, and from 10 to 25 wt % of a heterogeneous ethylene/alpha-olefincopolymer having a density of from 0.915 to 0.925 g/cm³. In combinationtherewith, the first inner layer may comprise a blend of (a) from 60 to95 wt % of at least one member selected from the group consisting ofpolyamide 6 and polyamide 6/66, and (b) from 5 to 40 wt % of polyamide6I/6T. In combination therewith, the second inner layer may comprise (i)from 50 to 70 wt % of an anhydride-functional ethylene/alpha-olefincopolymer, (ii) from 20 to 40 wt % anhydride-functionalstyrene/butadiene block copolymer; and (iii) from 5 to 15 wt %polyester. In combination therewith, the third inner layer may comprisesaponified ethylene vinyl acetate copolymer. In combination therewith,the fourth inner layer may comprise an anhydride-graftedethylene/alpha-olefin copolymer. In combination therewith, the fifthinner layer may comprise a blend of (i) from 60 to 95 wt % of at leastone member selected from the group consisting of polyamide 6 andpolyamide 6/66, and (ii) from 5 to 40 wt % of polyamide 6I/6T.

In an embodiment, the first outer layer makes up from 5 to 15 volume %based on total film volume, the second outer layer makes up from 15 to25 volume % based on total film volume, the first inner layer makes upfrom 10 to 20 volume % based on total film volume, the second innerlayer makes up from 10 to 20 volume % based on total film volume, thethird inner layer makes up from 2 to 10 volume % based on total filmvolume, the fourth inner layer makes up from 20 to 30 volume % based ontotal film volume, and the fifth inner layer makes up from 10 to 20volume % based on total film volume.

A seventh aspect is directed to a process for making a fully coextruded,heat-shrinkable annular film. The process comprises (I) coextrudingthrough an annular die film layers (A), (B), (C), and (D), i.e., thelayers according to the sixth aspect, (II) quenching the extrudate,(III) reheating the extrudate, and (IV) orienting the extrudate. Thequenching (II) of the annular extrudate is carried out by applying aquenching liquid to the annular extrudate. The reheating (III) of theextrudate is carried out by reheating the extrudate to an orientationtemperature of from 130° F. to 210° F., resulting in a reheated annularextrudate. The orientation (IV) of the annular extrudate is carried outby orienting the reheated annular extrudate while the reheated annularextrudate is in the solid state, the orientation being carried out witha total orientation factor of at least 2, so that an oriented,multilayer, heat-shrinkable film is produced. The orientation is carriedout so that the oriented, multilayer heat-shrinkable film exhibits atotal free shrink at 85° C. of at least 40 percent measured inaccordance with a modified free shrink test otherwise in accordance withASTM D 2732. The first polyester is present in the film in an amount ofat least 5 volume %, based on total film volume. The extrusion can becarried out in accordance with any of the embodiments of the sixthaspect described herein.

In an embodiment, the coextrusion can include layers (A), (B), (C), and(D) in combination with layer (E). In an alternative embodiment, thecoextrusion can include layers (A), (B), (C), and (D) in combinationwith layers (E), (F), and (G).

In an embodiment, the orientation is carried out with a totalorientation factor of at least 5, or at least 6, or at least 7, or atleast 8. The total orientation factor is the orientation factor in themachine direction multiplied by the orientation factor in the transversedirection. For example, if the reheated extrudate is stretched 2.5× inthe machine direction and 2.7× in the transverse direction, the totalorientation factor is about 6.75×.

In an embodiment, the quenching liquid absorbs heat from the annularextrudate as at least 50% of the quenching liquid cascades down theannular extrudate for a distance of at least 2 inches, with thequenching liquid making initial contact with the annular extrudate at adistance of from 0.1 to 8 inches downstream of a point at which theannular extrudate emerges from the annular die.

An eighth aspect is directed to a packaging process comprising: (A)providing a strand of a flat, heat-shrinkable, multilayer film inaccordance the sixth aspect, described above; (B) utilizing the film ina flow wrap process to produce a partially packaged product comprising abackseamed packaging article having a bottom seal and an open top, thepackaging article having a product therein; (C) evacuating atmospherefrom within the packaging article and sealing the open top of thepackaging article closed so that the product is surrounded by thepackaging article; and (D) shrinking the packaging article around theproduct.

In an embodiment, the process is carried out intermittently, and thepackaging article has a first portion of the backseam made beforeprocess interruption and a second portion of the backseam made afterprocess interruption.

A ninth aspect is directed to a packaging article made from a filmaccording to the sixth aspect. The packaging article is a memberselected from the group consisting of end-seal bag, side-seal bag,L-seal bag, and pouch.

A tenth aspect is directed to a packaged product comprising a packagingarticle made from a film according to the sixth aspect. The packagingarticle surrounds a product comprising food. In an embodiment, thepackaging article is in accordance with the ninth aspect.

THE BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic plan view of an end-seal bag.

FIG. 2 is a transverse cross-sectional view of the end-seal bag of FIG.1, taken through section 2-2 of FIG. 1.

FIG. 3 is a schematic plan view of a side-seal bag.

FIG. 4 is a transverse cross-sectional view of the side-seal bag of FIG.3, taken through section 4-4 of FIG. 3.

FIG. 5 is a schematic plan view of an L-seal bag.

FIG. 6 is a transverse cross-sectional view of the L-seal bag of FIG. 5,taken through section 6-6 of FIG. 5.

FIG. 7 is a longitudinal cross-sectional view of the L-seal bag of FIG.5, taken through section 7-7 of FIG. 5.

FIG. 8 is a schematic plan view of a backseamed bag having a fin-typebackseam.

FIG. 9 is a transverse cross-sectional view of the backseamed bag ofFIG. 8.

FIG. 10 is a schematic plan view of a backseamed bag having a lap-typebackseam.

FIG. 11 is a transverse cross-sectional view of the backseamed bag ofFIG. 10.

FIG. 12 is a schematic plan view of a pouch-type bag.

FIG. 13 is a transverse cross-sectional view of the pouch-type bag ofFIG. 12, taken through section 13-13 of FIG. 12.

FIG. 14 is a longitudinal cross-sectional view of the pouch-type bag ofFIG. 12, taken through section 14-14 of FIG. 12.

FIG. 15 is a schematic of a process used to make a heat-shrinkable filmsuch as could be used to make a heat-shrinkable bag or for use in a flowwrap packaging process.

FIG. 16 is a schematic of horizontal flow wrap process for packagingproducts using a heat shrinkable film in accordance with the invention.

DETAILED DESCRIPTION

As used herein, the term “film” is used in a generic sense to includeplastic web, regardless of whether it is film or sheet. Preferably,films of and used in the present invention have a thickness of 0.25 mmor less. The film can have any total thickness desired, so long as thefilm provides the desired properties for the particular packagingoperation in which the film is used.

As used herein, the term “package” refers to packaging materials used inthe packaging of a product, as well as the form that the film has beenplaced into in the preparation of the packaging article that partiallyor fully surrounds the product inside. As used herein, the phrase“packaged product” refers to the package having the product therein.

As used herein, the phrases “seal layer”, “sealing layer”, “heat seallayer”, and “sealant layer”, refer to an outer layer, or layers,involved in the sealing of the film to itself, another layer of the sameor another film, and/or another article which is not a film. Although itshould also be recognized that up to the outer 3 mils of a film can beinvolved in the sealing of the film to itself or another layer, thephrase “seal layer,” and the like, refer herein only to the outerlayer(s) which is to be heat-sealed to itself, another film, etc. Anyinner layers which contribute to the sealing performance of the film areherein designated as “seal-assist” layers. With respect to packageshaving only fin-type seals, as opposed to lap-type seals, the phrase“sealant layer” generally refers to the inside layer of a package, theinside layer being an outer layer which frequently also serves as a foodcontact layer in the packaging of foods

Sealant layers employed in the packaging arts have included the genus ofthermoplastic polymer, which includes thermoplastic polyolefin,polyamide, polyester, polyvinyl chloride, and ionomer resin. For lowtemperature end use, preferred polymers for the sealant layer includelow melt point polymers such as homogeneous ethylene/alpha-olefincopolymer, heterogeneous ethylene/alpha-olefin copolymer, ethylenehomopolymer, ethylene/vinyl acetate copolymer, and ionomer resin.

As used herein, the term “heat-seal,” and the phrase “heat-sealing,”refer to any seal of a first region of a film surface to a second regionof a film surface, wherein the seal is formed by heating the regions toat least their respective seal initiation temperatures. The heating canbe performed by any one or more of a wide variety of manners, such asusing a heated bar, hot wire, hot air, infrared radiation, ultrasonicsealing, etc. Heat-sealing is the process of joining two or morethermoplastic films or sheets by heating areas in contact with eachother to the temperature at which fusion occurs, usually aided bypressure. Heat-sealing is inclusive of thermal sealing, melt-beadsealing, impulse sealing, dielectric sealing, and ultrasonic sealing.

As used herein, the term “barrier,” and the phrase “barrier layer,” asapplied to films and/or layers, is used with reference to the ability ofa film or layer to serve as a barrier to one or more gases. The phrase“thermoplastic oxygen barrier” refers to any thermoplastic polymericmaterial which controls the oxygen permeability of the entire film. In amultilayer oxygen barrier film, the layer providing the lowest oxygentransmission rate (OTR) controls the oxygen barrier property of theentire film. For perishable food packaging applications, the OTR shouldbe minimized.

In the packaging arts, oxygen barrier layers (i.e., O₂ barrier layers)layers can include, for example, saponified ethylene/vinyl acetatecopolymer (also referred to as ethylene/vinyl alcohol copolymer, i.e.,EVOH), polyvinylidene chloride (PVDC), polyalkylene carbonate,polyamide, polyethylene naphthalate, polyester, polyacrylonitrile, etc.,as known to those of skill in the art. In the film of the presentinvention, the O₂-barrier layer preferably comprises either EVOH orpolyvinylidene chloride. PVDC can comprise a thermal stabilizer (i.e.,HCl scavenger, e.g., epoxidized soybean oil) and a lubricatingprocessing aid, which, for example, comprises one or more acrylates.

The phrase “oxygen transmission rate” (“OTR”) is defined herein as theamount of oxygen (O₂) in cubic centimeters (cm³) which will pass througha 100 square inches of film in 24 hours at 0% relative humidity and at23° C. The thickness (gauge) of the O₂-barrier layer has a directrelationship on the oxygen transmission rate. Packaging films which areuseful as an oxygen barrier are required to have an OTR value of fromabout 0 to 10.0 cm³/100 in² over 24 hr at 0% relative humidity and 23°C. at 1.0 mils or less. OTR can be measured according to ASTM D-3985-81,which is incorporated herein by reference.

In all of the aspects and embodiments set forth above, the thermoplasticoxygen barrier of the film may include, but is not limited to,ethylene/vinyl alcohol copolymer, polyamide, polyvinylidene chloride,and blends thereof. The thermoplastic oxygen barrier may be a blend ofpolyamides. The oxygen barrier layer may include a polyamide blend ofbetween about 85 wt % of a polyamide selected from the group consistingof nylon 4,6 (polytetramethylene adipamide), nylon 6 (polycaprolactam),nylon 6,6 (polyhexamethylene adipamide), nylon 6,9 (polyhexamethylenenonanediamide), nylon 6,10 (polyhexamethylene sebacamide), nylon 6,12(polyhexamethylene dodecanediamide), nylon 6/12 copolymer(polycaprolactam/dodecanediamide), nylon 6,6/6 copolymer(polyhexamethylene adipamide/caprolactam), nylon 11(polyundecanolactam), nylon 12 (polyauryllactam) or blends thereof, andabout 15 wt % of an amorphous polyamide.

As used herein, the phrase “ethylene/vinyl alcohol copolymer” or EVOH,refers to polymerized ethylene vinyl alcohol. Ethylene/vinyl alcoholcopolymer is saponified or hydrolyzed ethylene/vinyl acrylate copolymer.In all of the aspects and embodiments set forth above, the degree ofhydrolysis can be at least 50%, or at least 85%. The ethylene/vinylalcohol copolymer can comprise from about 28 to 48 mole % ethylene, orfrom about 32 to 44 mole % ethylene, or from about 38 to 44 mole %ethylene.

As used herein, the phrase “tie layer” refers to any internal layerhaving the primary purpose of adhering two film layers to one another.Tie layers can be used to adhere the barrier layer (such as EVOH) to apolyolefin heat seal layer, or to adhere a polyamide layer to apolyolefin layer. Such tie layers can comprise any polymer having apolar group grafted thereon. Polymers for use in tie layers for bondingpolyolefin to polyamide or EVOH include, but are not limited to:modified and unmodified ethylene/unsaturated acid copolymer, modifiedand unmodified ethylene/unsaturated ester copolymer, anhydride-graftedpolyolefin, polyurethane, modified and unmodified acrylate basedpolymer, and mixtures thereof.

Tie layers for bonding polyester to EVOH or PVDC or polyamide orpolyolefin include: modified or unmodified styrene-based polymers aloneor in blends with unsaturated ester copolymer (particularly unsaturatedacrylate copolymer) and/or cyclic olefin copolymer and optionallyfurther blended with anhydride modified polyolefin and/or polyester.

As used herein, the term “adhesive” refers to a polymeric materialserving a primary purpose or function of adhering two surfaces to oneanother. In the present invention, the adhesive may adhere one filmlayer surface to another film layer surface or one area of a film layersurface to another area of the same film layer surface. The adhesive maycomprise any polymer, copolymer or blend of polymers having a polargroup thereon, or any other polymer, homopolymer, copolymer or blend ofpolymers including modified and unmodified polymers, e.g., graftedcopolymers, which provide sufficient interlayer adhesion to adjacentlayers comprising otherwise nonadhering polymers. Adhesive compositionsof the present invention may include, but are not limited to, modifiedand unmodified polyolefins, including homopolymers and copolymers ofethylene, ethylene/α-olefin copolymer, modified and unmodified acrylatecopolymers such as ethylene/vinyl acrylate copolymer, ethylene/methylacrylate copolymer, ethylene/butyl acrylate copolymer, ethylene/ethylacrylate, or blends thereof.

As used herein, the term “adhered” is inclusive of films which aredirectly adhered to one another using a heat-seal or other means, aswell as films which are adhered to one another using an adhesive whichis between the two films. As used herein, the phrase “directly adhered”,as applied to layers, is defined as adhesion of the subject layer to theobject layer, without a tie layer, adhesive, or other layertherebetween. In contrast, as used herein, the word “between”, asapplied to a layer expressed as being between two other specifiedlayers, includes both direct adherence of the subject layer between tothe two other layers it is between, as well as including a lack ofdirect adherence to either or both of the two other layers the subjectlayer is between, i.e., one or more additional layers can be imposedbetween the subject layer and one or more of the layers the subjectlayer is between.

As used herein, the phrases “anhydride functional polymer” and “modifiedpolymer”, as well as more specific phrases such as “modifiedethylene/vinyl acetate copolymer,” “modified polyolefin,” and “anhydridefunctional styrene copolymer” refer to such polymers as have ananhydride functionality associated therewith, regardless of whether theanhydride functionality is grafted thereon and/or copolymerizedtherewith and/or blended therewith. Modified polymers can have theanhydride functionality grafted on or polymerized therewith, as opposedto merely blended therewith.

As used herein, the term “modified” refers to a chemical derivative,e.g. one having any form of anhydride functionality, such as anhydrideof maleic acid, crotonic acid, citraconic acid, itaconic acid, fumaricacid, etc., whether grafted onto a polymer, copolymerized with apolymer, or blended with one or more polymers, and is also inclusive ofderivatives of such functionalities, such as acids, esters, and metalsalts derived therefrom.

The anhydride functionality can be an anhydride of maleic acid, crotonicacid, citraconic acid, itaconic acid, fumaric acid, etc., and isinclusive of derivatives of such functionalities, such as acids, esters,and metal salts derived therefrom. As used herein, the phrase“anhydride-containing polymer” and “anhydride-modified polymer”, referto one or more of the following: (i) polymers obtained by copolymerizingan anhydride-containing monomer with a second, different monomer, and(ii) anhydride grafted copolymers, and (iii) a mixture of a polymer andan anhydride-containing compound.

As used herein, the phrase “acrylate-based resin” refers tohomopolymers, copolymers, including e.g. bipolymers, terpolymers, etc.,having an acrylate moiety in at least one of the repeating units (i.e.,“mer” units) forming the backbone of the polymer. Acrylate-based resinsinclude polyalkyl acrylates. Acrylate-based resins can be prepared byany method known to those skill in the art. Suitable examples of theseresins for use in the present invention include ethylene/vinyl acrylatecopolymers (EVA), ethylene/methacrylate copolymers (EMA), ethylene/butylacrylate copolymers (EBA), and the like.

As used herein, the phrase “styrene-based polymer” refers to at leastone polymer selected from the group consisting ofstyrene-ethylene-butylene-styrene copolymer, styrene-butadiene-styrenecopolymer, styrene-isoprene-styrene copolymer,styrene-ethylene-butadiene-styrene copolymer, andstyrene-(ethylene-propylene rubber)-styrene copolymer. As used herein,the phrase “styrene-based polymer” includes anhydride modifiedcopolymers of all styrene-based polymers identified herein. Unlessotherwise indicated, as used herein the use of a “dash” (i.e., the “-”)in a styrene-based polymer formula, is inclusive of both blockcopolymers and random copolymers. More particularly, the phrase“styrene-based polymer” includes both copolymers in which (i) all namedmonomers are present as a block, or (ii) any subset of the namedmonomers are present as a block with the remaining monomers beingrandomly arranged, or (Hi) all named monomers are randomly arranged.

Styrene-based polymers include hydrogenated block copolymers including:(a) polystyrene-poly(ethylene-propylene) diblock copolymer, e.g., KRATONG1701 and G1702 from Kraton Polymers; (b)polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer,e.g., KRATON G1641, G1650, G1651, G1654, G1657, G1726, G4609, G4610,GRP-6598, RP-6924, MD-6932M, MD-6933, and MD-6939 from Kraton Polymers;(c) polystyrene-poly(ethylene-butylene-styrene)-polystyrene (S-EB/S-S)triblock copolymer, e.g., KRATON RP-6935 and RP-6936 from KratonPolymers; (d) polystyrene-poly(ethylene-propylene)-polystyrene triblockcopolymer, e.g., KRATON G1730 from Kraton Polymers; (e) maleicanhydride-grafted polystyrene-poly(ethylene-butylene)-polystyrenetriblock copolymer, e.g., KRATON G1901, G1924, and MD-6684, from KratonPolymers; and (f) maleic anhydride-graftedpolystyrene-poly(ethylene-butylene-styrene)-polystyrene triblockcopolymer, e.g., KRATON MD-6670 from Kraton Polymers.

Further styrene-based hydrogenated block copolymers include: (g)polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer, suchas polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymercomprising 67 weight percent polystyrene available from Asahi KaseiElastomer as TUFTEC H1043; (h)polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer, suchas polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymercomprising 42 weight percent polystyrene available from Asahi KaseiElastomer as TUFTEC H1051; (i)polystyrene-poly(butadiene-butylene)-polystyrene triblock copolymer,such as TUFTEC P1000 and P2000 from Asahi Kasei Elastomer as; (j)polystyrene-polybutadiene-poly(styrene-butadiene)-polystyrene blockcopolymer, such as S.O.E.-SS L601 from Asahi Kasei Elastomer asS.O.E.-SS L601; (k) hydrogenated radial block copolymer, such as K-ResinKK38, KR01, KR03, and KR05 from Chevron Phillips Chemical Company as;(1) polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer,such as polystyrene-poly(ethylene-butylene)-polystyrene triblockcopolymer comprising 60 weight polystyrene available from Kuraray asSEPTON 58104; (m)polystyrene-poly(ethylene-ethylene/propylene)-polystyrene triblockcopolymer, such as SEPTON S4044, S4055, S4077, and S4099 from Kuraray;(n) polystyrene-poly(ethylene-propylene)-polystyrene triblock copolymer,such as polystyrene-poly(ethylene-propylene)-polystyrene triblockcopolymer comprising 65 weight percent polystyrene available fromKuraray as SEPTON S2104. Mixtures of two of more hydrogenated blockcopolymers can be used.

As used herein, the phrase “compatibilizing layer” refers to a filmlayer that has its first principal surface directly adhered to a primarylayer, with its second principal surface offering greater bond strengthfor direct bonding with a tertiary layer than if the tertiary layer wasto be directly bonded to the primary layer. A compatibilizing layer ispresent in many of the films of Table 2 below. The compatibilizing layercontains a blend of 90% polyamide 6/66 and 10% polyamide 6I/6T. A firstprincipal surface of the compatibilizing layer is directly adhered tothe barrier layer, which is EVOH in the films of Table 2. The secondprincipal surface of the compatibilizing layer is directly adhered to atie layer made from a modified linear low density polyethylene. The bondbetween the modified linear low density polyethylene and the polyamideblend is stronger than the bond strength that would have been present ifthe modified linear low density polyethylene was bonded to the EVOH. Assuch, the compatibilizing layer enhances the interlaminar strengthwithin the multilayer film, but need not be a thick layer, as itscompatibilizing advantage is based on chemistry, not bulk.

As used herein, the term “oriented” refers to a polymer-containingmaterial which has been stretched at an elevated temperature (theorientation temperature), followed by being “set” in the stretchedconfiguration by cooling the material while substantially retaining thestretched dimensions. Upon subsequently heating unrestrained,unannealed, oriented polymer-containing material to its orientationtemperature, heat shrinkage is produced almost to the originalunstretched, i.e., pre-oriented dimensions. More particularly, the term“oriented”, as used herein, refers to oriented films, wherein theorientation can be produced in one or more of a variety of manners.

As used herein, the phrase “orientation ratio” refers to themultiplication product of the extent to which the plastic film materialis expanded in several directions, usually two directions perpendicularto one another. Expansion in the machine direction is herein referred toas “drawing”, whereas expansion in the transverse direction is hereinreferred to as “stretching”. For films extruded through an annular die,stretching is usually obtained by “blowing” the film to produce abubble. For such films, drawing is usually obtained by passing the filmthrough two sets of powered nip rolls, with the downstream set having ahigher surface speed than the upstream set, with the resulting drawratio being the surface speed of the downstream set of nip rolls dividedby the surface speed of the upstream set of nip rolls. The degree oforientation is also referred to as the orientation ratio, or sometimesas the “racking ratio”.

As used herein, the phrase “machine direction”, herein abbreviated “MD”,refers to a direction “along the length” of the film, i.e., in thedirection of the film as the film is formed during extrusion and/orcoating. As used herein, the phrase “transverse direction”, hereinabbreviated “TD”, refers to a direction across the film, perpendicularto the machine or longitudinal direction.

As used herein, the phrases “heat-shrinkable,” “heat-shrink,” and thelike, refer to the tendency of a film, generally an oriented film, toshrink upon the application of heat, i.e., to contract upon beingheated, such that the size (area) of the film decreases while the filmis in an unrestrained state. Likewise, the tension of a heat-shrinkablefilm increases upon the application of heat if the film is restrainedfrom shrinking. As a corollary, the phrase “heat-contracted” refers to aheat-shrinkable film, or a portion thereof, which has been exposed toheat such that the film or portion thereof is in a heat-shrunken state,i.e., reduced in size (unrestrained) or under increased tension(restrained).

As used herein, the phrase “free shrink” refers to the percentdimensional change in a 10 cm. by 10 cm. specimen of film, whensubjected to selected heat (i.e., at a certain temperature), with thequantitative determination being carried out according to ASTM D 2732,as set forth in the 1990 Annual Book of ASTM Standards, Vol. 08.02,pages 368-371, which is hereby incorporated, in its entirety, byreference thereto. As used herein, the phrase “@STP” refers to the testbeing carried out under standardized test conditions, i.e., oneatmosphere of pressure, 23° C., and 0% relative humidity.

Although the above free shrink test disclosed above is a standard ASTMfree shrink test for use in assessing the degree of shrinkage exhibitedby a heat shrinkable film, the free shrink of the films of the Table 2,and the free shrink values recited in the claims below, were measured bya “a modified free shrink test otherwise in accordance with ASTM D2732.”The modified test was carried out because of the tendency of the film tocurl during the free shrink test, making measurement difficult due todifficulty of measuring the uncurled film sample after shrinking.

The modified free shrink test otherwise in accordance with ASTM D2732was carried out by marking a sample with a 10 cm by 10 cm square andthen cutting the sample so that the entire sample had a 25 mm borderoutside of the 10 cm marking. That is, the sample was 15 cm by 15 cmwith the central 10 cm by 10 cm being marked out before shrinking. Theshrinking was carried out otherwise in accordance with ASTM D2732,except that percent free shrink in each direction was calculated bymeasuring the marked area after shrinking, rather than measuring thefull sample dimensions after shrinking. In all other regards, the actualshrinking of the sample was conducted as per ASTM D2732, but the shrinkmeasurement was made by measuring the marking after shrinking, with theexcess film being utilized to hold the film during unrolling, so thatthe film could be held flat for the post-shrink measurement to be taken.

As used herein, the phrase “heat-shrinkable” is used with reference toall films which exhibit a total free shrink (i.e., L+T) of at least 10percent at 85° C.

“Total free shrink” is determined by summing the percent free shrink inthe machine direction with the percentage of free shrink in thetransverse direction. For example, a film which exhibits, at 85° C., 30percent free shrink in the transverse direction and 20 percent freeshrink in the machine direction, has a “total free shrink” at 85° C. of50 percent.

As used herein, the term “monomer” refers to a relatively simplecompound, usually containing carbon and of low molecular weight, whichcan react to form a polymer by combining with itself or with othersimilar molecules or compounds.

As used herein, the term “comonomer” refers to a monomer which iscopolymerized with at least one different monomer in a copolymerizationreaction, the result of which is a copolymer.

As used herein, the term “polymer” refers to the product of apolymerization reaction, and is inclusive of homopolymers, copolymers,terpolymers, etc. A film layer can consist of a single polymer (with orwithout non-polymeric additives), or can have still additional polymerstogether therewith, i.e., blended therewith.

As used herein, the term “homopolymer” is used with reference to apolymer resulting from the polymerization of a single monomer, i.e., apolymer consisting essentially of a single type of mer, i.e., repeatingunit.

As used herein, the term “copolymer” refers to polymers formed by thepolymerization reaction of at least two different monomers. For example,the term “copolymer” includes the copolymerization reaction product ofethylene and an alpha-olefin, such as 1-hexene. However, the term“copolymer” is also inclusive of, for example, the copolymerization of amixture of ethylene, propylene, 1-hexene, and 1-octene. The termcopolymer is also inclusive of polymers produced by reaction, such asgraft copolymer, block copolymer, and random copolymer.

As used herein, the term “polymerization” is inclusive ofhomopolymerizations, copolymerizations, terpolymerizations, etc., andincludes all types of copolymerizations such as random, graft, block,etc. Polymers in the films used in accordance with the presentinvention, can be prepared in accordance with any suitablepolymerization process, including slurry polymerization, gas phasepolymerization, and high pressure polymerization processes.

As used herein, the term “copolymerization” refers to the simultaneouspolymerization of two or more monomers to result in a copolymer. As usedherein, a copolymer identified in terms of a plurality of monomers,e.g., “propylene/ethylene copolymer”, refers to a copolymer in whicheither monomer may copolymerize in a higher weight or molar percent thanthe other monomer or monomers. However, the first listed monomerpreferably polymerizes in a higher weight percent than the second listedmonomer, and, for copolymers which are terpolymers, quadripolymers,etc., preferably the first monomer copolymerizes in a higher weightpercent than the second monomer, and the second monomer copolymerizes ina higher weight percent than the third monomer, etc.

For addition polymers, copolymers are identified, i.e., named, in termsof the monomers from which the copolymers are produced. For example, thephrase “propylene/ethylene copolymer” refers to a copolymer produced bythe copolymerization of both propylene and ethylene, with or withoutadditional comonomer(s). A copolymer comprises recurring “mers” derivedfrom the monomers from which the copolymer is produced, e.g., apropylene/ethylene copolymer comprises propylene mer units and ethylenemer units.

As used herein, terminology employing a “/” with respect to the chemicalidentity of a copolymer (e.g., “an ethylene/alpha-olefin copolymer”),identifies the comonomers which are copolymerized to produce thecopolymer. As used herein, “ethylene alpha-olefin copolymer” is theequivalent of “ethylene/alpha-olefin copolymer.”

As used herein, the term “polyester” refers to homopolymers orcopolymers having an ester linkage between monomer units which may beformed, for example, by condensation polymerization reactions between adicarboxylic acid and a glycol. The dicarboxylic acid may be linear oraliphatic, i.e., oxalic acid, malonic acid, succinic acid, glutaricacid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacicacid, and the like; or may be aromatic or alkyl substituted aromatic,e.g., various isomers of phthalic acid (i.e., ortho-phthalic acid), suchas isophthalic acid (i.e., meta-phthalic acid), and terephthalic acid(i.e., para-phthalic acid), as well as naphthalic acid. Specificexamples of alkyl substituted aromatic acids include the various isomersof dimethylphthalic acid, such as dimethylisophthalic acid,dimethylorthophthalic acid, dimethylterephthalic acid, the variousisomers of diethylphthalic acid, such as diethylisophthalic acid,diethylorthophthalic acid, the various isomers of dimethylnaphthalicacid, such as 2,6-dimethylnaphthalic acid and 2,5-dimethylnaphthalicacid, and the various isomers of diethylnaphthalic acid. Thedicarboxylic acid can alternatively be 2,5-furandicarboxylic acid(FDCA). The glycols may be straight-chained or branched. Specificexamples include ethylene glycol, propylene glycol, trimethylene glycol,1,4-butane diol, neopentyl glycol and the like. The glycols includemodified glycols such as cyclohexane dimethanol. The polyester in theouter layer of the film can comprise any of the above polyesters. Thefirst layer can comprise polyethylene terephthalate copolymer,polybutylene terephthalate, polynaphthalene terephthalate, and/orpolyethylene furanoate, any of which can be biaxially-oriented. As usedherein, the term “polyester” is inclusive of both polyethyleneterephthalate homopolymer as well as copolymers thereof.

In an embodiment the outer layer comprises polyethylene furanoate.Avantium® bio-based polyester is a polyethylene furanoate which per unitthickness exhibits only one tenth the oxygen transmission rate ofpolyethylene terephthalate (PET); one fourth the carbon dioxidetransmission rate of PET, and one half the water vapor transmission rateof PET. Polyethylene furanoate is more heat resistant than PET (T_(g)12° C. higher than PET. Furthermore, polyethylene furanoate isrecyclable alone or in a blend with PET. Polyethylene furanoate can beextruded to form films. Polyethylene furanoate is made by polymerizingethylene glycol and 2,5-furandicarboxylic acid (FDCA). Polyethylenefuranoate renewable because it is bio-based.

As used herein, the term “polyamide” refers to homopolymers, copolymers,or terpolymers having an amide linkage between monomer units which maybe formed by any method known to those skill in the art. Usefulpolyamide homopolymers include nylon 6 (polycaprolactam), nylon 11(polyundecanolactam), nylon 12 (polylauryllactam), and the like. Otheruseful polyamide homopolymers also include nylon 4,2 (polytetramethyleneethylenediamide), nylon 4,6 (polytetramethylene adipamide), nylon 6,6(polyhexamethylene adipamide), nylon 6,9 (polyhexamethylene azelamide),nylon 6,10 (polyhexamethylene sebacamide), nylon 6,12 (polyhexamethylenedodecanediamide), nylon 7,7 (polyheptamethylene pimelamide), nylon 8,8(polyoctamethylene suberamide), nylon 9,9 (polynonamethylene azelamide),nylon 10,9 (polydecamethylene azelamide), nylon 12,12(polydodecamethylene dodecanediamide), and the like. Useful polyamidecopolymers include nylon 6,6/6 copolymer (polyhexamethyleneadipamide/caprolactam copolymer), nylon 6/6,6 copolymer(polycaprolactam/hexamethylene adipamide copolymer), nylon 6,2/6,2copolymer (polyhexamethylene ethylenediamide/hexamethyleneethylenediamide copolymer), nylon 6,6/6,9/6 copolymer (polyhexamethyleneadipamide/hexamethylene azelaiamide/caprolactam copolymer), as well asother nylons which are not particularly delineated here. Additionalpolyamides include nylon 4,1, nylon 6,1, nylon 6,6/6I copolymer, nylon6,6/6T copolymer, MXD6 (poly-m-xylylene adipamide), nylon 6T/6Icopolymer, nylon 6/MXDT/I copolymer, nylon MXDI, poly-p-xylyleneadipamide, polyhexamethylene terephthalamide, polydodecamethyleneterephthalamide and the like.

The multilayer heat shrinkable film can have a polyamide layer made upof any one or more of the polyamides in the paragraph above. Moreover,the polyamide can be blended with another polymer, such as ionomerresin, polyether block amide copolymer (e.g., PEBAX® polyether blockamide), maleic anhydride grafted polymer (e.g., grafted ethyleneacrylate carbon monoxide terpolymer, grafted ethylene vinyl acetate,grafted heterogeneous polyethylene, grafted homogeneous (e.g.,metallocene catalyzed) polyethylene, grafted ethylene propylene rubber,and grafted polypropylene, grafted styrene butadiene copolymer, andgrafted styrene ethylene butylene styrene copolymer. Moreover, thepolyamide or polyamide blend can make up at least 60 wt % of the layer,based on layer weight, or at least 80 wt % based on layer weight, or atleast 90 wt % based on layer weight, or at least 95 wt % based on layerweight, or 100 wt % based on layer weight.

As used herein, the phrase “amorphous polyamide” refers to polyamides ornylons with an absence of a regular three-dimensional arrangement ofmolecules or subunits of molecules extending over distances, which arelarge relative to atomic dimensions. However, regularity of structureexists on a local scale. See, “Amorphous Polymers,” in Encyclopedia ofPolymer Science and Engineering, 2nd Ed., pp. 789-842 (J. Wiley & Sons,Inc. 1985). This document has a Library of Congress Catalogue CardNumber of 84-19713. In particular, the term “amorphous polyamide” refersto a material recognized by one skilled in the art of differentialscanning calorimetry (DSC) as having no measurable melting point (lessthan 0.5 cal/g) or no heat of fusion as measured by DSC using ASTM3417-83. Such nylons include those amorphous nylons prepared fromcondensation polymerization reactions of diamines with dicarboxylicacids. For example, an aliphatic diamine is combined with an aromaticdicarboxylic acid, or an aromatic diamine is combined with an aliphaticdicarboxylic acid to give suitable amorphous nylons. As used herein, thephrase “amorphous polyamide” includes (i) the copolymer of hexamethylenediamine and isophthalic acid and terphthalic acid, i.e., polyamide 6I6T,and (ii) the homopolymer of meta-xylene diamine and adipic acid, i.e.,polyamide MXD6.

As used herein, the phrase “heterogeneous polymer” refers topolymerization reaction products of relatively wide variation inmolecular weight and relatively wide variation in compositiondistribution, i.e., typical polymers prepared, for example, usingconventional Ziegler-Natta catalysts. Heterogeneous polymers are usefulin various layers of the film used in the present invention. Althoughthere are a few exceptions (such as TAFMER™ linear homogeneousethylene/alpha-olefin copolymers produced by Mitsui PetrochemicalCorporation, using Ziegler-Natta catalysts), heterogeneous polymerstypically contain a relatively wide variety of chain lengths andcomonomer percentages.

As used herein, the phrase “homogeneous polymer” refers topolymerization reaction products of relatively narrow molecular weightdistribution and relatively narrow composition distribution. Homogeneouspolymers are useful in various layers of the multilayer film used in thepresent invention. Homogeneous polymers are structurally different fromheterogeneous polymers, in that homogeneous polymers exhibit arelatively even sequencing of comonomers within a chain, a mirroring ofsequence distribution in all chains, and a similarity of length of allchains, i.e., a narrower molecular weight distribution. Furthermore,homogeneous polymers are typically prepared using metallocene, or othersingle-site type catalysis, rather than using Ziegler Natta catalysts.

More particularly, homogeneous ethylene/alpha-olefin copolymers may becharacterized by one or more methods known to those of skill in the art,such as molecular weight distribution (M_(w)/M_(n)), compositiondistribution breadth index (CDBI), and narrow melting point range andsingle melt point behavior. The molecular weight distribution(M_(w)/M_(n)), also known as polydispersity, may be determined by gelpermeation chromatography. The homogeneous ethylene/alpha-olefincopolymers useful in this invention generally have an M_(w)/M_(n) ofless than 2.7; preferably from about 1.9 to about 2.5; more preferably,from about 1.9 to about 2.3. The composition distribution breadth index(CDBI) of such homogeneous ethylene/alpha-olefin copolymers willgenerally be greater than about 70 percent. The CDBI is defined as theweight percent of the copolymer molecules having a comonomer contentwithin 50 percent (i.e., plus or minus 50%) of the median total molarcomonomer content. The CDBI of linear polyethylene, which does notcontain a comonomer, is defined to be 100%. The Composition DistributionBreadth Index (CDBI) is determined via the technique of TemperatureRising Elution Fractionation (TREF). CDBI determination clearlydistinguishes the homogeneous copolymers used in the present invention(narrow composition distribution as assessed by CDBI values generallyabove 70%) from VLDPEs available commercially which generally have abroad composition distribution as assessed by CDBI values generally lessthan 55%. The CDBI of a copolymer is readily calculated from dataobtained from techniques known in the art, such as, for example,temperature rising elution fractionation as described, for example, inWild et. al., J. Poly. Sci. Poly. Phys. Ed., Vol. 20, p. 441 (1982).Preferably, the homogeneous ethylene/alpha-olefin copolymers have a CDBIgreater than about 70%, i.e., a CDBI of from about 70% to about 99%. Thehomogeneous ethylene/alpha-olefin copolymers in the multilayer films tobe used in the present invention also exhibit a relatively narrowmelting point range, in comparison with “heterogeneous copolymers”,i.e., polymers having a CDBI of less than 55%. Preferably, thehomogeneous ethylene/alpha-olefin copolymers exhibit an essentiallysingular melting point characteristic, with a peak melting point(T_(m)), as determined by Differential Scanning Colorimetry (DSC), offrom about 60° C. to about 105° C. Preferably the homogeneous copolymerhas a DSC peak T_(m) of from about 80° C. to about 100° C. As usedherein, the phrase “essentially single melting point” means that atleast about 80%, by weight, of the material corresponds to a single Tmpeak at a temperature within the range of from about 60° C. to about105° C., and essentially no substantial fraction of the material has apeak melting point in excess of about 115° C., as determined by DSCanalysis. DSC measurements are made on a Perkin Elmer System 7 ThermalAnalysis System. Melting information reported are second melting data,i.e., the sample is heated at a programmed rate of 10° C./min. to atemperature below its critical range. The sample is then reheated (2ndmelting) at a programmed rate of 10° C./min. The presence of highermelting peaks is detrimental to film properties such as haze, andcompromises the chances for meaningful reduction in the seal initiationtemperature of the final film.

A homogeneous ethylene/alpha-olefin copolymer can be prepared by thecopolymerization of ethylene and any one or more alpha-olefins.Preferably, the alpha-olefin is a C₃₋₂₀ α-monoolefin, more preferably, aC₄₋₁₂ α-monoolefin, still more preferably, a C₄₋₈ α-monoolefin. Stillmore preferably, the alpha-olefin comprises at least one member selectedfrom the group consisting of butene-1, hexene-1, and octene-1, i.e.,1-butene, 1-hexene, and 1-octene, respectively. Most preferably, thealpha-olefin comprises octene-1, and/or a blend of hexene-1 andbutene-1.

Processes for preparing and using homogeneous polymers are disclosed inU.S. Pat. Nos. 5,206,075, 5,241,031, and PCT International ApplicationWO 93/03093, each of which is hereby incorporated by reference thereto,in its entirety. Further details regarding the production and use ofhomogeneous ethylene/alpha-olefin copolymers are disclosed in PCTInternational Publication Number WO 90/03414, and PCT InternationalPublication Number WO 93/03093, both of which designate Exxon ChemicalPatents, Inc. as the Applicant, and both of which are herebyincorporated by reference thereto, in their respective entireties.

Still another genus of homogeneous ethylene/alpha-olefin copolymers isdisclosed in U.S. Pat. No. 5,272,236, to LAI, et. al., and U.S. Pat. No.5,278,272, to LAI, et. al., both of which are hereby incorporated byreference thereto, in their respective entireties.

As used herein, terms identifying polymers, such as “polyamide”,“polyester”, “polyurethane”, etc. are inclusive of not only polymerscomprising repeating units derived from monomers known to polymerize toform a polymer of the named type, but are also inclusive of comonomers,derivatives, etc. which can copolymerize with monomers known topolymerize to produce the named polymer, including modified polymerssuch as anhydride modified polymers. For example, the term “polyamide”encompasses both polymers comprising repeating units derived frommonomers, such as caprolactam, which polymerize to form a polyamide, aswell as copolymers derived from the copolymerization of caprolactam witha comonomer which when polymerized alone does not result in theformation of a polyamide. Furthermore, terms identifying polymers arealso inclusive of mixtures, blends, etc. of such polymers with otherpolymers of a different type.

As used herein, the phrase “cyclic polymer” includes cyclic olefincopolymer, whether aliphatic or phenolic, i.e., includingethyleneinorbornene copolymer, polycyclododecene, polyester, and cyclicolefin polymer.

As used herein, the term “polyolefin” refers to any polymerized olefin,which can be linear, branched, cyclic, aliphatic, aromatic, substituted,or unsubstituted. More specifically, included in the term polyolefin arehomopolymers of olefin, copolymers of olefin, copolymers of an olefinand an non-olefinic comonomer copolymerizable with the olefin, such asvinyl monomers, modified polymers thereof, and the like. Specificexamples include polyethylene homopolymer, polypropylene homopolymer,polybutene, ethylene/alpha-olefin copolymer, ethylene/propylenecopolymer, propylene/alpha-olefin copolymer, butene/alpha-olefincopolymer, low density polyethylene, linear low density polyethylene,very low density polyethylene, ultra low density polyethylene, mediumdensity polyethylene, high density polyethylene, polyethylenescomprising copolymers of ethylene with one or more alpha-olefins(α-olefins) such as butene-1, hexene-1, octene-1, or the like as acomonomer, linear low density polyethylene, very low densitypolyethylene, ultra low density polyethylene, ethylene/propylenecopolymers, polypropylene, propylene/ethylene copolymer, polyisoprene,polybutylene, polybutene, poly-3-methylbutene-1, poly-4-methylpentene-1,ethylene/unsaturated ester copolymer, ethylene/unsaturated acidcopolymer, (especially ethyl acrylate copolymer, ethylene/butyl acrylatecopolymer, ethylene/methyl acrylate copolymer, ethylene/acrylic acidcopolymer, ethylene/methacrylic acid copolymer), modified polyolefinresin, ionomer resin, polymethylpentene, etc. Modified polyolefin resinis inclusive of modified polymer prepared by copolymerizing thehomopolymer of the olefin or copolymer thereof with an unsaturatedcarboxylic acid, e.g., maleic acid, fumaric acid or the like, or aderivative thereof such as the anhydride, ester or metal salt or thelike. It could also be obtained by incorporating into the olefinhomopolymer or copolymer, an unsaturated carboxylic acid, e.g., maleicacid, fumaric acid or the like, or a derivative thereof such as theanhydride, ester or metal salt or the like.

As used herein, the phrase “ethylene alpha-olefin copolymer”, and“ethylene/alpha-olefin copolymer”, refer to such heterogeneous materialsas linear low density polyethylene (LLDPE), and very low and ultra lowdensity polyethylene (VLDPE and ULDPE); and homogeneous polymers such asmetallocene-catalyzed EXACT™ linear homogeneous ethylene/alpha olefincopolymer resins obtainable from the Exxon Chemical Company, of Baytown,Tex., and TAFMER™ linear homogeneous ethylene/alpha-olefin copolymerresins obtainable from the Mitsui Petrochemical Corporation. All thesematerials generally include copolymers of ethylene with one or morecomonomers selected from C₄₋₁₀ α-olefin such as butene-1 (i.e.,1-butene), hexene-1, octene-1, etc. in which the molecules of thecopolymers comprise long chains with relatively few side chain branchesor cross-linked structures. This molecular structure is to be contrastedwith conventional low or medium density polyethylenes which are morehighly branched than their respective counterparts. The heterogeneousethylene/alpha-olefin commonly known as LLDPE has a density usually inthe range of from about 0.91 grams per cubic centimeter to about 0.94grams per cubic centimeter. Other ethylene/alpha-olefin copolymers, suchas the long chain branched homogeneous ethylene/alpha-olefin copolymersavailable from The Dow Chemical Company, known as AFFINITY™ resins, arealso included as another type of homogeneous ethylene/alpha-olefincopolymer useful in the present invention.

The ethylene/alpha-olefin copolymer comprises a copolymer resulting fromthe copolymerization of from about 80 to about 99 weight percentethylene and from 1 to about 20 weight percent alpha-olefin. Preferably,the ethylene/alpha-olefin copolymer comprises a copolymer resulting fromthe copolymerization of from about 85 to about 95 weight percentethylene and from about 5 to about 15 weight percent alpha-olefin.

As used herein, the phrases “inner layer” and “internal layer” refer toany layer, of a multilayer film, having both of its principal surfacesdirectly adhered to another layer of the film.

As used herein, the phrase “outer layer” refers to any layer of filmhaving less than two of its principal surfaces directly adhered toanother layer of the film. The phrase is inclusive of monolayer andmultilayer films. In multilayer films, there are two outer layers, eachof which has a principal surface adhered to only one other layer of themultilayer film. In monolayer films, there is only one layer, which, ofcourse, is an outer layer in that neither of its two principal surfacesare adhered to another layer of the film.

As used herein, the phrase “inside layer” refers to the outer layer, ofa multilayer film packaging a product, which is closest to the product,relative to the other layers of the multilayer film. “Inside layer” alsois used with reference to the innermost layer of a plurality ofconcentrically arranged layers simultaneously coextruded through anannular die.

As used herein, the phrase “outside layer” refers to the outer layer, ofa multilayer film packaging a product, which is furthest from theproduct relative to the other layers of the multilayer film. The phrase“outside layer” also is used with reference to the outermost layer of aplurality of concentrically arranged layers coextruded through anannular die.

As used herein, the term “extrusion” is used with reference to theprocess of forming continuous shapes by forcing a molten plasticmaterial through a die, followed by cooling or chemical hardening.Immediately prior to extrusion through the die, the relativelyhigh-viscosity polymeric material is fed into a rotating screw ofvariable pitch, i.e., an extruder, which forces the polymeric materialthrough the die.

As used herein, the term “coextrusion” refers to the process ofextruding two or more materials through a single die with two or moreorifices arranged so that the extrudates merge and weld together into alaminar structure before chilling, i.e., quenching. Coextrusion can beemployed in film blowing, free film extrusion, and extrusion coatingprocesses.

The multilayer heat-shrinkable film of the invention can be fullycoextruded, in contrast to being the lamination of two films produced byseparate extrusion processes. In a fully coextruded film, all layers ofthe film are extruded simultaneously. A fully coextruded film is free oflamination adhesive, with the layers of the film being melt bonded toone another.

At least a portion of the multilayer film of the present invention canoptionally be irradiated to induce crosslinking. In the irradiationprocess, the film is subjected to one or more energetic radiationtreatments, such as corona discharge, plasma, flame, ultraviolet, X-ray,gamma ray, beta ray, and high energy electron treatment, each of whichinduces cross-linking between molecules of the irradiated material. Theirradiation of polymeric films is disclosed in U.S. Pat. No. 4,064,296,to BORNSTEIN, et. al., which is hereby incorporated in its entirety, byreference thereto. BORNSTEIN, et. al. discloses the use of ionizingradiation for crosslinking the polymer present in the film.

To produce crosslinking, a suitable radiation dosage of high energyelectrons is employed, preferably using an electron accelerator, with adosage level being determined by standard dosimetry methods. Otheraccelerators such as a Van de Graaf or resonating transformer may beused. The radiation is not limited to electrons from an acceleratorsince any ionizing radiation may be used. The ionizing radiation can beused to crosslink the polymers in the film. Preferably, the film isirradiated at a level of from about 30 kGy to about 207 kGy, morepreferably from about 30 kGy to about 140 kGy. As can be seen from thedescriptions of preferred films for use in the present invention, themost preferred amount of radiation is dependent upon the film and itsend use.

As used herein, the phrases “corona treatment” and “corona dischargetreatment” refer to subjecting the surfaces of thermoplastic materials,such as polyolefins, to corona discharge, i.e., the ionization of a gassuch as air in close proximity to a film surface, the ionizationinitiated by a high voltage passed through a nearby electrode, andcausing oxidation and other changes to the film surface, such as surfaceroughness.

Corona treatment of polymeric materials is disclosed in U.S. Pat. No.4,120,716, to BONET, issued Oct. 17, 1978, herein incorporated in itsentirety by reference thereto. BONET discloses improved adherencecharacteristics of the surface of polyethylene by corona treatment, tooxidize the polyethylene surface. U.S. Pat. No. 4,879,430, to HOFFMAN,also hereby incorporated in its entirety by reference thereto, disclosesthe use of corona discharge for the treatment of plastic webs for use inmeat cook-in packaging, with the corona treatment of the inside surfaceof the web to increase the adhesion of the meat to the adhesion of themeat to the proteinaceous material. The films of this invention can becorona-treated in a preferred embodiment.

FIG. 1 is a schematic of a preferred end-seal bag 10, in a lay-flatposition; FIG. 2 is a cross-sectional view of bag 10 taken throughsection 2-2 of FIG. 1. Viewing FIGS. 1 and 2 together, bag 10 comprisesbag film 11, top edge 12 defining an open top, first bag side edge 13,second bag side edge 14, bottom edge 15, and end seal 16.

FIGS. 3 and 4 illustrate side-seal bag 18. FIG. 3 illustrates aschematic of side seal bag 18, in a lay-flat view; FIG. 4 illustrates across-sectional view taken through section 4-4 of FIG. 3. With referenceto FIGS. 3 and 4 together, side seal bag 18 is comprised of bag film 19,top edge 20 defining an open top, bottom edge 21, first side seal 22,and second side seal 23.

FIG. 5 is a lay-flat view of a preferred L-seal bag 26, in a lay-flatposition. FIG. 6 is a transverse cross-sectional view of L-seal bag 26,taken through section 6-6 of FIG. 5. FIG. 7 is a longitudinalcross-sectional view of L-seal bag 26 taken through section 7-7 of FIG.5. Viewing FIGS. 5, 6, and 7 together, L-seal bag 26 has side-seal 28,bottom seal 30, open top 32, seamless folded bag side edge 34, andseamed bag side edges 36.

The fin-seal backseamed bag 38 of FIGS. 8 and 9 has open top 40, bottomseal 42, first folded side edge 44, second folded side edge 46, bottomedge 48, backseam seal 50 (inside film layer heat sealed to itself), andbackseam fins 52.

The lap-seal backseamed bag 54 of FIGS. 10 and 11 has open top 55,bottom seal 56, first folded side edge 58, second folded side edge 60,bottom edge 62, and backseam seal 64 (inside film layer heat sealed tooutside film layer).

FIGS. 12, 13, and 14 illustrate a pouch-type bag 66 made from sealingtwo separate pieces of flat film together. In FIGS. 12, 13, and 14,pouch 66 has open top 68, bottom heat seal 70 and bottom edge 72, firstside seal 74 and first side edge 76, second side seal 78 and second sideedge 80. Together, first and second side seals 74 and 76 connect withbottom seal 70 to form a “U-shaped” seal connecting the two pieces offlat film together to form the pouch-type bag 66.

The process illustrated in FIG. 15 can be used to make multilayerheat-shrinkable film for use in the packaging articles of FIGS. 1-14,described above. In FIG. 15, solid polymer beads (not illustrated) arefed into a plurality of extruders 100. For simplicity, only one extruder100 is illustrated in FIG. 15. Inside each extruder 100, polymer beadsare forwarded, melted, and degassed, following which the resultingstream of bubble-free melt emitted from each extruder 100 is forwardedinto annular multilayer die 102.

The melt streams from extruders 100 are fed into multilayer annular die102, pass through multilayer annular die 102, and are emitted fromannular die 102 in the form of discrete layers, resulting in annularmultilayer extrudate 104, also referred to as a “tape.” The number ofextruders 100 may correspond with the number of discrete layers inmultilayer annular extrudate 104, or may be less than the number of filmlayers if the extrudate from a single extruder 100 is split into two ormore streams, with each stream being used to form a discrete layer ofmultilayer annular extrudate 104.

As annular extrudate 104 emerges from annular die 102, annular extrudate104 passes inside calibrator 106, which is positioned below annular die102 so that the upper edge of calibrator 106 is about 2 to 2.5 inchesbelow the point at which annular extrudate 104 emerges from annular die102. Calibrator 106 has a length of from 12 to 18 inches. Calibrator 106is essentially a pipe with an outside surface and an inside surface. Theinside surface controls the diameter of extrudate 104. Moreover,calibrator 106 provides quenching liquid to annular extrudate 104, ascalibrator 106 is itself hollow and is connected to a source of coldwater (not illustrated) which is pumped inside the walls of calibrator106 from a chiller (not illustrated). A plurality of annular slots (notillustrated) in the inside surface of calibrator 106 feed streams ofcold water between the inside surface of calibrator 106 and the outsidesurface of annular extrudate 104, in order to quench annular extrudate104 as it emerges from annular die 102. In the making of the films inTable 2, below, calibrator 106 was supplied with 43° C. water, which waslikely 46° C. to 48° C. before the water contacted annular extrudate104. Calibrator 106 serves to control the size of the outside diameterof annular extrudate 104, as well as the quenching of annular extrudate104.

Calibrator 106, as well as about four feet of the uppermost portion ofannular extrudate 104, are surrounded by vacuum chamber 108.Supplemental cold water sprayers 110 are provided inside vacuum chamber108. Vacuum chamber 108 is connected to a source of vacuum (notillustrated). The bottom edge of vacuum chamber 108 is provided withsealing ring 112 so that water emitted from the slots in calibrator 106,as well as water from sprayers 110, can be evacuated away, recirculatedthrough the chiller, and recycled back into calibrator 106 sprayers 110.

Collapse of annular extrudate 104 is prevented by maintaining a slightsuperatmospheric pressure inside annular extrudate via centrallypositioned pipe 114 passing through the center of annular die 102, andextending downward from annular die 102. Alternatively, or in additionto maintaining a slight positive pressure inside annular extrudate 104(i.e., inside the “first bubble”), a slight vacuum, i.e., 15-18millibars, is maintained by evacuating water and atmosphere from theinternal region 116 inside vacuum chamber 108. In this manner, thediameter of annular extrudate 104 is closely controlled while thethermoplastic resins emitted from annular die 102 are quenched uponextrusion. Moreover the rate of extrusion of resin from annular die 102,in combination with control over the downward speed of annular extrudate104 by governance of the surface speed of nip rollers 118, determinesthe amount of necking down of annular extrudate 104 as it emerges fromannular die 102. Extrusion rate and roller surface speed were controlledso that annular extrudate 104 has an outside diameter appropriate forthe internal diameter of calibrator 106.

Annular extrudate 104 moves downward into water bath 120, and iscollapsed into lay-flat configuration as it passes through nip rollers118 within water bath 120. The resulting lay-flat tubing 122 emergesfrom water bath 120 and passes over idler rollers 124 and 126, and thenthrough optional irradiation chamber 128 and around idler roller 130,and then through upper nip rollers 132. Annular extrudate 104 can remainat an elevated temperature at the time it reaches nip rollers 132 (e.g.,a ° C._(t) of from 73° C. to 93° C. in Table 2 below).

Immediately upon passing through upper nip rollers 132, annularextrudate 122 is re-inflated to its extruded diameter (i.e., a firstportion of the “second bubble”) as it passes through four sets ofheaters 134 positioned around the entirety of annular extrudate 136.Heaters 134 progressively heat inflated annular extrudate 136 to itssoftening point (e.g., a ° C._(b) of from 56° C. to 130° C. in Table 2below), after which inflated, softened annular extrudate 138 passesthrough a set of supporting guide rollers 140. Guide rollers 140maintain inflated annular extrudate 136 and bubble 142 in a centralposition in the oven, so that annular extrudate 136 and bubble 142 canbe heated evenly by the various heaters surrounding the second bubble.After passing through guide rollers 140, annular extrudate 138 is blowninto oriented bubble 142 (i.e., the second portion of the secondbubble).

The entirety of the second bubble contains trapped air 144 between uppernip rollers 132 and lower nip rollers 146. Lower nip rollers 146 have asurface speed higher than upper nip rollers 132, thereby stretchingsoftened extrudate 138 in the machine direction. Moreover, the greaterdiameter of oriented bubble 142 provides transverse solid stateorientation of extrudate 138. Three sets of supplemental heaters 147 areprovided along oriented bubble 142. The result is biaxially orientedfilm tubing 148 at the downstream end of oriented bubble 142.

Thereafter, lower nip rollers 146 collapse biaxially oriented filmtubing 148 into a lay-flat configuration, with the resulting lay-flattubing 150 passing over idler rollers 152 and 154, and through niprollers 156, after which lay-flat tubing 150 is reinflated into thirdbubble 158 which surrounds trapped air 160. Trapped air 160 ismaintained inside third bubble 158 by upper nip rollers 156 and lowernip rollers 164. As the biaxially oriented film of bubble 158 passesdownward, it is annealed by three sets of infrared annealing heaterssurrounding bubble 158. The surface speed of upper nip rollers 156 isabout the same as the surface speed of lower nip rollers 164. Uponpassing through lower nip rollers 164, the resulting biaxially oriented,annealed film 166 is returned to lay-flat configuration, and is woundupon roll 168.

FIG. 16 illustrates the use of a heat-shrinkable film, such as the filmsof Table 2, below. The process illustrated in FIG. 16 is a type ofhorizontal form fill and seal process known in the packaging art as a“flow wrap” process. The process of FIG. 16 utilizes a continuous rollof flat film to package a product in a packaging article as illustratedin FIGS. 8 and 9 (or FIGS. 10 and 11), rather than pre-made bags orpouches as illustrated in FIGS. 1-9 and 12-14.

Although the process of FIG. 16 is at least theoretically capable ofbeing run continuously, in actual use the process is intermittent, withdifferent packagers having different frequency and duration of processinterruption. The process of FIG. 16 does not produce a fully closedpackage. Rather, the product of the packaging operation illustrated inFIG. 16 results in a product inside the open packaging articleillustrated in FIGS. 8-9 (described above), with the product inside theopen packaging article being forwarded downstream to further machinery(described below) for completion of the packaging process.

In FIG. 16, products 302 are fed to packaging machine 303 via conveyor304. Although product 302 can be any product to be packaged, a preferredproduct is a meat product, such as a roast, steak, chops, ribs, etc.Each product 302 can be an individual piece of meat or a set comprisinga plurality of pieces of meat.

Conveyor 304 terminates as the input end of forming horn 306. Product302 is pushed into forming horn 306 by a pusher (not illustrated).Product 302 is pushed onto the upper surface of continuous strand offilm 308 as product 302 is pushed into and through forming horn 306.Continuous strand of film 308 (supplied from a roll of film, notillustrated) is forwarded into, through, and past forming horn 306 as acontinuous stream of products 302 are individually pushed into forminghorn 306. Once on film 308, products 302 are forwarded through forminghorn 306 by the forwarding of the strand of film 308, i.e., at the samespeed that film 308 passes into, through, and beyond forming horn 306.Once on film 308, the forwarding of film 308 forwards products 302therewith.

Film 308 is folded as it passes through forming horn 306, so that asproduct 302 emerges from forming horn 306, film 308 is folded aroundproduct 302, with product 302 now being inside a tube 312 of film 308.Above forming shoe 306, the edges of film 308 are folded upward and asealing apparatus (not illustrated) forms a continuous fin-type heatseal 310 along the upwardly folded longitudinal edges of film 308. Theheat seal can be formed using, for example, three sets of seal heads,i.e., three sets of heat sealing nip rollers. The first set (upstream)of heat sealing nip rollers can have a temperature of 65° C. The secondset (middle) of heat sealing nip rollers can have a temperature of 90°C. The third set (downstream) of heat sealing nip rollers can have atemperature of 150° C. The head pressure of the seat heads was 2 bar.The web speed was 17.2 meters per minute. During the formation ofbackseam heat seal 310, film 308 surrounding products 302 is forwardedby a second conveyor (not illustrated) on which film 308 and products302 rest.

During process interruption in which the flow of products is temporarilyhalted, the seal heads are pulled away from the film so that the film isnot burned by a long period of contact with the hot seal heads. Uponresumption of the process, seal heads are reapplied to the film and thebackseaming is continued. Of course, it is desirable that the package beprovided with a strong backseam seal even if a portion of the backseamseal was made before process interruption and a portion of the backseamseal was made after process resumption. It is desirable that such apackage exhibit a burst strength at least 95 percent as high as theburst strength of a package made from the same film but in which thebackseam seal was continuously produced, i.e., without interruption.Alternatively, the package having a backseam with portions made beforeand after process interruption can have a burst strength of at least 90percent, or at least 85 percent, or at least 80 percent, or at least 75percent as high as the burst strength of a corresponding package inwhich the backseam was continuously produced, i.e., withoutinterruption.

The stream of products 302 inside now sealed film tubing 312 isforwarded to a transverse sealer and cutter including uppersealer/cutter member 314 and lower sealer/cutter member 316, which worktogether to make transverse seals between products 302, and to cut filmtubing 312 apart to produce individual packaged products 318. Thetemperatures for each of the two transverse seal bars in members 314 and316 may be, for example, 105° C. and 105° C. with the seal bar dwelltime being, for example, 350 milliseconds. Upper and lower sealer/cutterbars 314, 316 oscillate upward and downward as film tubing 312 isforwarded. Upon being sealed on the downstream end and cut free of thebackseamed film tubing, the result is partially packaged product 318having a backseam down its length, a closed bottom seal, and an open topend, as illustrated in FIGS. 8 and 9, described above.

Upon exiting packaging machine 303, partially packaged products 318 areforwarded to a vacuum chamber machine in which atmosphere is evacuatedfrom inside the package and the open end of the package is heat sealedclosed, so that the product is completely surrounded by the heatshrinkable packaging article. The resulting evacuated, closed packagedproduct is thereafter forwarded to a shrink machine in which the film isshrunk against the product by passing the evacuated, closed packagedproduct through a hot air tunnel or by immersing the evacuated, closedpackaged product in a bath of hot water.

The process of FIG. 16 is but one embodiment of the manner in which thefilm can be used. The process of FIG. 16 is called “flow wrap” and is atype of process known in the art as “horizontal form fill and seal.”When used in conjunction with downstream vacuum packaging, it isreferred to as a “flow vac process.” The film can also be used invertical form fill and seal packaging, as described in U.S. Pat. No.5,491,019, to Kuo, which is hereby incorporated, in its entirety, byreference thereto. The film can be used to make packaging articles suchas bags and pouches, including the bags and pouches illustrated in FIGS.1 through 14.

EXAMPLES

The present invention can be further understood by reference to thefollowing examples that are merely illustrative and are not to beinterpreted as a limitation to the scope of the present invention thatis defined by the appended claims. The films of the examples containedvarious resins identified in Table 1, below.

TABLE 1 Tradename/ Resin Supplier Chemical Nature Properties &Parameters LLDPE Dowlex ® 2045.03 Linear Low Density Polyethylene 0.920g/cm³ Dow (Ziegler Natta catalyzed) 1.1 g/10 min 6.5 wt % octene merEt-Cop ELVALOY ® PTW ethylene copolymer 0.94 g/cc 12 g/10 min 72° C. mpsscPE-1 Affinity ® PL 1850G Single site catalyzed polyethylene 0.902g/cc Dow 3.0 g/10 min 97° C. mp sscPE-2 Affinity ® PF 1140G Single sitecatalyzed ethylene 0.896 g/cc; Dow copolymer 1.6 g/10 min 94° C. mpsscPE-3 Affinity ® PL 1281G1 Single site catalyzed 0.900 g/cc; Dowethylene/octene copolymer 6.0 g/10 min 99° C. mp sscPE-4 EXCEED ® 4518PASingle site catalyzed 0.92 g/cc; ExxonMobil ethylene/hexene copolymer4.5 g/10 min 116° C. mp EVA Escorene ® LD713.93 Ethylene vinyl acetatecopolymer 0.933 g/cc; Exxon Mobil 3.5 g/10 min 87° C. mp EVA-2 ELVAX ®3182-2 Ethylene vinyl acetate copolymer 0.95 g/cc; DuPont 3.0 g/10 min74° C. mp; 28 wt % vinyl acetate EMA SP2260 EMA Copolymer Ethylenemethyl acrylate 0.944 g/cc; Westlake Chemical copolymer 77° C. mp 24%methyl acrylate EMA-2 EMAC + SP1330 Ethylene methyl acrylate 0.944 g/cc;Westlake Chemical copolymer 2 g/10 min; mp 93° C. 22% methyl acrylateEMA-3 Lotoader AX 8900 Ethylene methyl acrylate 0.91 g/cc Arkemacopolymer EMA-4 Elvaloy AC 1224 Ethylene methyl acrylate 0.94 g/cc;DuPont copolymer 2 g/10 min; mp 91° C. 20% methyl acrylate mEMA Bynel ®CXA 21E787 Maleic anhydride modified 0.93 g/cc; DuPont ethylene/methylacrylate copolymer 1.6 g/10 min; 92° C. mp EBA SP 1903 Ethylene butylacrylate copolymer 18% butyl acrylate; Westlake Chemical 0.928 g/cc;0.45 g/10 min mLLD-1 Plexar ® PX 3227 Maleic anhydride modified LLDPE0.913 g/cm³ Nippon Goshei 1.7 g/10 min mLLD-2 Admer ® AT2754A Maleicanhydride modified 0.900 g/cc; Mitsui Petrochemical polyethylene 2.0g/10 min 96° C. mp mLLD-3 Amplify ® GR216 Anhydride modified linear low0.875 g/cc; 1.3 mfi Dow density polyethylene 62.8° C. mp SEC MD-6932M(G1643 MS) Styrene/ethylene copolymer 0.9 g/cc; Kraton Polymers 1.8 g/10min SBC Styroflex ® 2G 66 Styrene/butadiene copolymer - 0.99 g/cc; BASFStyrene/butadiene/styrene 12.5 g/10 min tribiock copolymer SBC-2FG1901GT Styrene butadiene multiblock 0.91 g/cc; Kraton Polymerscopolymer 22 g/10 min SBC-3 FG1924 Styrene butadiene multiblock Meltindex: Kraton Polymers copolymer 40 (230 C./5 Kg) g-SEBS KRATON ®FG1901G maleic anhydride-grafted linear 0.91 g/cc; Kraton PolymersStyrene/ethylene/butylene 22 g/10 min Triblock copolymer 230° C. meltpoint (styrene/rubber 30/70) ENB TOPAS ® 9903D-10 Ethylene/norbornenecopolymer 0.974 g/cc; Topas Advanced Polymers, 1.0 g/10 min Inc. PA 6ULTRAMID ® B40 Polyamide 6 1.13 g/cc BASF 220° C. melt point PA6/66Ultramid ® C33 01 Polyamide 6/66 1.13 g/cm³ BASF 196° C. melt pointPA6I/6T Grivory ® G21 Natural Polyamide 6I/6T 1.18 g/cc; EMS GrivoryT_(g) 125° C. PAMXD6 MXD6 Nylon S6007 Polyamide MXD6 1.22 g/ccMitsubishi Eng. - Plastics 237° C. mp PET-1 Eastapak ® Copolyester 9921copolyester 1.40 g/cc Eastman Chemical 255° C. mp PET-2 Eastapak ® 32897APET copolyester 1.3 g/cc Eastman Chemical PET-3 Vitel 1901NSB-Pcopolyester 1.23 g/cc Bostik Intrinsic viscosity of: 0.92 dl/g; meltpoint 121° C. PET-4 Arnitel L-X07110 Polyester 1.25 g/cc DSM PETGEastar ® PETG 6763 Polyethylene terephthalate/glycol 1.27 g/cc EastmanChemical 2.8 g/10 min EVOH-1 Eval ® XEP-1232 Hydrolyzed ethylene vinyl1.15 g/cc; Evalca/Kuraray acetate (EVOH) 1.5 g/10 min 38% ethyleneEVOH-2 Eval ® SP292B Hydrolyzed ethylene vinyl 1.14 g/cc; Evalca/Kurarayacetate copolymer (EVOH) 2.1 g/10 min 44% ethylene EVOH-3 XEP-1321BHydrolyzed ethylene vinyl 1.15 g/cc; Evalca/Kuraray acetate copolymer(EVOH) 4.0 g/10 min 38% ethylene; mp 148° C. EVOH-4 Soranol ® ET3803Ethylene vinyl alcohol copolymer 1.17 g/cc; Nippon Goshei containing 38%ethylene 3.2 g/10 min 173° C. melt point S&AB 1070SB Slip and Antiblockin LLDPE 0.98 g/cc; Ingenia Polymers 5.5 g/10 min 122° C. mp S&AB-210853 Antiblock Silica in LLDPE 1.00 g/cc; Ampacet 1.5 g/10 min 122° C.mp PETME T Me S606 Crosslinker additive 6% SiO₂; 10% wax; 0.8 SukanoMelt enhancer for polyester g/cc; 1.2 g/cc; 0.5% moisture; 82° C. vicatsoftening pointThe resins identified in Table 1, above, were used in the preparation ofthe films of Table 2, below. The films of Table 2, below, were preparedusing the process illustrated in FIG. 15, described above.

TABLE 2 Work Film or Layer 1 No. comp (inside) Layer 2 Layer 3 Layer 4Layer 5 Layer 6 1 C 80% sscPE-1 mLLD-2 90% PA6/66 EVOH-1 mEMA mEMA 15%LLDPE (0.11 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) (0.08 mil) 5% S&AB(0.05 mil) (0.55 mil) 2 C 80% sscPE-1 mLLD-2 90% PA6/66 EVOH-1 mEMA mEMA15% LLDPE (0.11 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) (0.08 mil) 5%S&AB (0.05 mil) (0.55 mil) 3 C 81% sscPE-1 mLLD-2 90% PA6/66 EVOH-4 mEMAPET-1 15% LLDPE (0.12 mil) 10% PA6I/6T (0.06 mil) (0.12 mil) (0.18 mil)4% S&AB (0.06 mil) (0.47 mil) 4 C 81% sscPE-1 mLLD-2 90% PA6/66 EVOH-4mEMA PET-1 15% LLDPE (0.12 mil) 10% PA6I/6T (0.06 mil) (0.12 mil) (0.18mil) 4% S&AB (0.06 mil) (0.47 mil) 5 C 81% sscPE-1 mLLD-2 90% PA6/66EVOH-4 mEMA PET-1 15% LLDPE (0.12 mil) 10% PA6I/6T (0.06 mil) (0.12 mil)(0.18 mil) 4% S&AB (0.06 mil) (0.47 mil) 6 C 81% sscPE-1 mLLD-2 90%PA6/66 EVOH-2 mEMA PET-1 15% LLDPE (0.16 mil) 10% PA6I/6T (0.08 mil)(0.16 mil) (0.24 mil) 4% S&AB (0.08 mil) (0.63 mil) 7 C 60% sscPE-1mLLD-2 90% PA6/66 EVOH-3 mEMA PET-1 15% LLDPE (0.16 mil) 10% PA6I/6T(0.08 mil) (0.16 mil) (0.31 mil) 20% EVA (0.08 mil) 5% S&AB (0.47 mil) 8C 70% sscPE-1 mLLD-2 90% PA6/66 EVOH-3 mEMA PET-1 15% LLDPE (0.16 mil)10% PA6I/6T (0.08 mil) (0.16 mil) (0.24 mil) 10% EVA (0.08 mil) 5% S&AB(0.63 mil) 9 C 80% sscPE-2 mLLD-2 90% PA6/66 EVOH-1 mEMA mEMA 15% LLDPE(0.11 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) (0.08 mil) 5% S&AB (0.05mil) (0.55 mil) 10 C 80% sscPE-2 mLLD-2 90% PA6/66 EVOH-3 mEMA PET-1 15%LLDPE (0.16 mil) 10% PA6I/6T (0.08 mil) (0.16 mil) (0.24 mil) 5% S&AB(0.08 mil) (0.63 mil) 11 C 80% sscPE-2 mLLD-2 90% PA6/66 EVOH-3 mEMAPET-1 15% LLDPE (0.16 mil) 10% PA6I/6T (0.08 mil) (0.16 mil) (0.24 mil)5% S&AB (0.08 mil) (0.63 mil) 12 C 80% sscPE-2 mLLD-2 90% PA6/66 EVOH-1mLLD-2 mEMA 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) (0.08mil) 5% S&AB (0.08 mil) (0.60 mil) 13 W 80% sscPE-2 mLLD-2 90% PA6/66EVOH-3 90% EMA PET-1 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) 10% SEC(0.33 mil) 5% S&AB (0.08 mil) (0.08 mil) (0.60 mil) 14 W 80% sscPE-2mLLD-2 90% PA6/66 EVOH-1 80% EMA PET-1 15% LLDPE (0.08 mil) 10% PA6I/6T(0.08 mil) 20% SEC (0.33 mil) 5% S&AB (0.08 mil) (0.08 mil) (0.60 mil)15 C 80% sscPE-1 mLLD-2 90% PA6/66 EVOH-3 mEMA PET-1 15% LLDPE (0.16mil) 10% PA6I/6T (0.08 mil) (0.16 mil) (0.33 mil) 5% S&AB (0.08 mil)(0.44 mil) PRO C 80% sscPE-1 mLLD-2 90% PA6/66 EVOH-3 mEMA PET-1 16 15%LLDPE (0.16 mil) 10% PA6I/6T (0.08 mil) (0.16 mil) (0.33 mil) 5% S&AB(0.08 mil) (0.44 mil) 17 C 80% sscPE-1 mLLD-2 90% PA6/66 EVOH-3 mEMAPET-1 15% LLDPE (0.16 mil) 10% PA6I/6T (0.08 mil) (0.16 mil) (0.33 mil)5% S&AB (0.08 mil) (0.44 mil) 18 C 85% sscPE-2 mLLD-2 90% PA6/66 EVOH-3mEMA PET-1 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.16 mil) (0.24mil) (0.71 mil) (0.08 mil) 19 — 85% sscPE-2 mLLD-2 90% PA6/66 EVOH-3mLLD-1 80% EMA 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.16 mil)20% SEC (0.71 mil) (0.08 mil) (0.24 mil) 20 — 85% sscPE-2 mLLD-2 90%PA6/66 EVOH-3 mLLD-1 80% EMA 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil)(0.16 mil) 20% SEC (0.71 mil) (0.08 mil) (0.24 mil) 21 — 85% sscPE-2mLLD-2 90% PA6/66 EVOH-3 mLLD-1 80% EMA 15% LLDPE (0.08 mil) 10% PA6I/6T(0.08 mil) (0.16 mil) 20% SEC (0.71 mil) (0.08 mil) (0.24 mil) 22 W 80%sscPE-2 mLLD-2 90% PA6/66 EVOH-3 mLLD-1 80% EMA 15% LLDPE (0.16 mil) 10%PA6I/6T (0.08 mil) (0.08 mil) 10% SEC 5% S&AB (0.08 mil) 10% mLLD-3(0.71 mil) (0.08 mil) 23 W 80% sscPE-2 mLLD-2 90% PA6/66 EVOH-3 mLLD-180% EMA 15% LLDPE (0.16 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 10% SEC5% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 24 W 80% sscPE-2mLLD-2 90% PA6/66 EVOH-3 mLLD-1 80% EMA 15% LLDPE (0.16 mil) 10% PA6I/6T(0.08 mil) (0.08 mil) 20% SEC 5% S&AB (0.08 mil) (0.08 mil) (0.71 mil)25 W PET-1 80% EMA mLLD-1 EVOH-3 90% PA6/66 mLLD-2 (0.47 mil) 10% SEC(0.08 mil) (0.08 mil) 10% PA6I/6T (0.08 mil) 10% mLLD-3 (0.08 mil) (0.08mil) 26 W PET-1 80% EMA mLLD-1 EVOH-3 90% PA6/66 mLLD-2 (0.47 mil) 10%SEC (0.08 mil) (0.08 mil) 10% PA6I/6T (0.08 mil) 10% mLLD-3 (0.08 mil)(0.08 mil) 27 W PET-1 80% EMA mLLD-1 EVOH-3 90% PA6/66 mLLD-2 (0.47 mil)10% SEC (0.08 mil) (0.08 mil) 10% PA6I/6T (0.08 mil) 10% mLLD-3 (0.08mil) (0.08 mil) 28 W PET-1 80% EMA mLLD-1 EVOH-3 90% PA6/66 mLLD-2 (0.47mil) 10% SEC (0.08 mil) (0.08 mil) 10% PA6I/6T (0.08 mil) 10% mLLD-3(0.08 mil) (0.08 mil) 29 W PET-1 80% EMA mLLD-1 EVOH-2 90% PA6/66 mLLD-2(0.47 mil) 10% SEC (0.08 mil) (0.08 mil) 10% PA6I/6T (0.08 mil) 10%mLLD-3 (0.08 mil) (0.08 mil) 30 W PET-1 80% EMA mLLD-1 EVOH-4 90% PA6/66mLLD-2 (0.47 mil) 10% SEC (0.08 mil) (0.08 mil) 10% PA6I/6T (0.08 mil)10% mLLD-3 (0.08 mil) (0.08 mil) 31 W PET-1 PET-1 80% EMA EVOH-2 90%PA6/66 mLLD-2 (0.24 mil) (0.24 mil) 10% SEC (0.08 mil) 10% PA6I/6T (0.08mil) 10% mLLD-3 (0.08 mil) (0.08 mil) 32 W PET-1 PET-1 80% EMA EVOH-2mLLD-2 sscPE-3 (0.24 mil) (0.24 mil) 10% SEC (0.08 mil) (0.08 mil) (0.16mil) 10% mLLD-3 (0.08 mil) 33 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-3mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil)10% SEC 3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 34 W 80%sscPE-3 mLLD-2 90% PA6/66 EVOH-3 mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10%PA6I/6T (0.08 mil) (0.08 mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3(0.71 mil) (0.08 mil) 35 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-3 mLLD-280% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 10% SEC3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 36 W 80% sscPE-3mLLD-2 90% PA6/66 EVOH-3 mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T(0.08 mil) (0.08 mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil)(0.08 mil) 37 W 85% sscPE-3 mLLD-2 90% PA6/66 EVOH-3 mLLD-2 80% EMA 15%LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 10% SEC (0.71 mil)(0.08 mil) 10% mLLD-3 (0.08 mil) 38 W 80% sscPE-3 mLLD-2 90% PA6/66EVOH-3 mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 39 W80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 80% EMA 17% LLDPE (0.08 mil)10% PA6I/6T (0.08 mil) (0.08 mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3(0.71 mil) (0.08 mil) 40 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-280% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 10% SEC3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 41 W 80% sscPE-3mLLD-2 90% PA6/66 EVOH-2 mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T(0.08 mil) (0.08 mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil)(0.08 mil) 42 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 80% EMA 17%LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 10% SEC 3% S&AB (0.08mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 43 W 80% sscPE-3 mLLD-2 90% PA6/66EVOH-2 mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil) (0.08 mil) 44 W80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 80% EMA PET-1 17% LLDPE (0.08 mil)10% PA6I/6T (0.08 mil) 10% SEC (0.08 mil) 3% S&AB (0.08 mil) 10% mLLD-3(0.71 mil) (0.08 mil) 45 W 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 80% EMAPET-1 17% LLDPE (0.08 mil) (0.08 mil) (0.08 mil) 10% SEC (0.08 mil) 3%S&AB 10% mLLD-3 (0.71 mil) (0.08 mil) 46 W 80% sscPE-3 sscPE-3 mLLD-2EVOH-2 80% EMA PET-1 17% LLDPE (0.08 mil) (0.08 mil) (0.08 mil) 10% SEC(0.08 mil) 3% S&AB 10% mLLD-3 (0.71 mil) (0.08 mil) 47 W 80% sscPE-3mLLD-2 90% PA6/66 EVOH-2 mLLD-2 80% EMA 17% LLDPE (0.08 mil) 10% PA6I/6T(0.08 mil) (0.08 mil) 10% SEC 3% S&AB (0.08 mil) 10% mLLD-3 (0.71 mil)(0.08 mil) 48 W 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 80% EMA PET-1 17%LLDPE (0.35 mil) (0.08 mil) (0.08 mil) 10% SEC (0.28 mil) 3% S&AB 10%mLLD-3 (0.43 mil) (0.09 mil) 49 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2mLLD-2 85% EMA 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil)15% SEC 5% S&AB (0.08 mil) (0.08 mil) (0.71 mil) 50 W 80% sscPE-3 mLLD-290% PA6/66 EVOH-3 mLLD-2 85% EMA 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08mil) (0.08 mil) 15% SEC 5% S&AB (0.08 mil) (0.08 mil) (0.71 mil) 51 —80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 mLLD-2 85% EMA 17% LLDPE (0.31 mil)(0.08 mil) (0.08 mil) (0.08 mil) 15% SEC 3% S&AB (0.08 mil) (0.47 mil)52 C 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 PAMXD6 PET-1 15% LLDPE (0.16 mil)(0.08 mil) (0.08 mil) (0.08 mil) (0.24 mil) 5% S&AB (0.71 mil) 53 W 80%sscPE-3 sscPE-3 mLLD-2 EVOH-2 80% EMA PET-1 17% LLDPE (0.44 mil) (0.15mil) (0.15 mil) 10% SEC (0.44 mil) 3% S&AB 10% mLLD-3 (0.61 mil) (0.15mil) 54 W 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 80% EMA PET-1 17% LLDPE(0.44 mil) (0.15 mil) (0.15 mil) 10% SEC (0.44 mil) 3% S&AB 10% mLLD-3(0.61 mil) (0.15 mil) 55 W 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 mLLD-2 80%EMA 17% LLDPE (0.14 mil) (0.13 mil) (0.11 mil) (0.14 mil) 10% SEC 3%S&AB 10% mLLD-3 (0.31 mil) (0.11 mil) 56 W 80% sscPE-3 sscPE-3 mLLD-2EVOH-2 mLLD-2 80% EMA 17% LLDPE (0.11 mil) (0.14 mil) (0.11 mil) (0.14mil) 10% SEC 3% S&AB 10% mLLD-3 (0.42 mil) (0.23 mil) 57 W 80% sscPE-3sscPE-3 mLLD-2 EVOH-2 mLLD-2 80% EMA 15% LLDPE (0.31 mil) (0.08 mil)(0.08 mil) (0.08 mil) 10% SEC 5% S&AB 10% mLLD-3 (0.47 mil) (0.08 mil)58 W 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 mLLD-2 80% EMA 15% LLDPE (0.31mil) (0.08 mil) (0.08 mil) (0.08 mil) 10% SEC 5% S&AB 10% mLLD-3 (0.47mil) (0.08 mil) 59 W 80% sscPE-3 sscPE-3 mLLD-2 EVOH-2 mLLD-2 80% EMA15% LLDPE (0.31 mil) (0.08 mil) (0.08 mil) (0.08 mil) 10% SEC 5% S&AB10% mLLD-3 (0.47 mil) (0.08 mil) 60 W 80% sscPE-3 mLLD-2 90% PA6/66EVOH-2 mLLD-2 SEC 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil)(0.08 mil) 5% S&AB (0.08 mil) (0.71 mil) 61 W 80% sscPE-3 mLLD-2 90%PA6/66 EVOH-2 mLLD-2 80% SEC 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil)(0.08 mil) 20% ENB 5% S&AB (0.08 mil) (0.08 mil) (0.71 mil) 62 W 80%sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 80% SBC 15% LLDPE (0.08 mil) 10%PA6I/6T (0.08 mil) (0.08 mil) 20% ENB 5% S&AB (0.08 mil) (0.08 mil)(0.71 mil) 63 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 90% SBC 15%LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 10% ENB 5% S&AB (0.08mil) (0.08 mil) (0.71 mil) 64 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2mLLD-2 65% SBC 15% LLDPE (0.52 mil) 10% PA6I/6T (0.13 mil) (0.13 mil)25% EMA 5% S&AB (0.13 mil) 10 PET-3 (0.77 mil) (0.29 mil) 65 W 80%sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 85% EMA 15% LLDPE (0.31 mil) 10%PA6I/6T (0.08 mil) (0.08 mil) 15% SEC 5% S&AB (0.08 mil) (0.08 mil)(0.47 mil) 66 — 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 85% EMA 15%LLDPE (0.55 mil) 10% PA6I/6T (014 mil) (0.14 mil) 15% SEC 5% S&AB (0.14mil) (0.14 mil)) (0.83 mil) 67 — 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2mLLD-2 85% SEC 15% LLDPE (0.08 mil) 10% PA6I/6T (0.08 mil) (0.08 mil)15% EMA 5% S&AB (0.08 mil) (0.08 mil) (0.71 mil) 68 — 80% sscPE-3 mLLD-290% PA6/66 EVOH-2 mLLD-2 75% SEC 15% LLDPE (0.55 mil) 10% PA6I/6T (0.14mil) (0.14 mil) 25% EMA 5% S&AB (0.14 mil) (0.14 mil) (0.83 mil) 69 W80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SEC 17% LLDPE (0.52 mil)10% PA6I/6T (0.13 mil) (0.13 mil) 25% EMA 3% S&AB (0.13 mil) 10% PET-3(0.77 mil) (0.29 mil) 70 — 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-290% SEC 15% LLDPE (0.55 mil) 10% PA6I/6T (0.14 mil) (0.14 mil) 10% PET-35% S&AB (0.14 mil) (0.14 mil) (0.83 mil) 71 — 80% sscPE-3 mLLD-2 90%PA6/66 EVOH-2 mEMA 90% SEC 15% LLDPE (0.55 mil) 10% PA6I/6T (0.14 mil)(0.14 mil) 10% PETME 5% S&AB (0.14 mil) (0.14 mil) (0.83 mil) 72 W 80%sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 85% EMA 15% sscPE-4 (0.31 mil)10% PA6I/6T (0.08 mil) (0.08 mil) 15% SEC 5% S&AB-2 (0.08 mil) (0.08mil) (0.47 mil) 73 C 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 EMA-215% LLDPE (0.52 mil) 10% PA6I/6T (0.13 mil) (0.13 mil) (0.29 mil) 5%S&AB (0.13 mil) (0.78 mil) 74 C 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2mLLD-2 PET-4 15% LLDPE (0.52 mil) 10% PA6I/6T (0.13 mil) (0.13 mil)(0.29 mil) 5% S&AB (0.13 mil) (0.78 mil) 75 W 80% sscPE-3 mLLD-2 90%PA6/66 EVOH-2 mLLD-2 90% SBC-3 15% LLDPE (0.52 mil) 10% PA6I/6T (0.13mil) (0.13 mil) 10% EMA-2 5% S&AB (0.13 mil) (0.29 mil) (0.78 mil) 76 W80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 90% SBC-2 15% LLDPE (0.52mil) 10% PA6I/6T (0.13 mil) (0.13 mil) 10% EMA-2 5% S&AB (0.13 mil)(0.29 mil) (0.78 mil) 77 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-250% SBC-3 15% LLDPE (0.52 mil) 10% PA6I/6T (0.13 mil) (0.13 mil) 25%EMA-2 5% S&AB (0.13 mil) 25% SEC (0.78 mil) (0.29 mil) 78 W 80% sscPE-3mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SEC 15% LLDPE (0.52 mil) 10% PA6I/6T(0.13 mil) (0.13 mil) 25% EMA-2 5% S&AB (0.13 mil) 10% SBC-3 (0.78 mil)(0.29 mil) 79 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SEC 15%LLDPE (0.47 mil) 10% PA6I/6T (0.14 mil) (0.14 mil) 25% EMA 5% S&AB (0.26mil) 10% PET-3 (0.69 mil) (0.29 mil) 80 W 80% sscPE-3 mLLD-2 90% PA6/66EVOH-2 90% PA6/66 50% SBC-2 15% LLDPE (0.52 mil) 10% PA6I/6T (0.14 mil)10% PA6I/6T 40% mEMA 5% S&AB (0.28 mil) (0.14 mil) 10% PET-3 (0.77 mil)(0.29 mil) 81 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 85% EMA 17%LLDPE (0.31 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 15% SEC 3% S&AB (0.08mil) (0.08 mil) (0.47 mil) 82 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2mLLD-2 65% SEC 17% LLDPE (0.29 mil) 10% PA6I/6T (0.08 mil) (0.08 mil)25% EMA 3% S&AB (0.08 mil) 10% PET-3 (0.44 mil) (0.17 mil) 83 W 80%sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SBC-2 17% LLDPE (0.29 mil)10% PA6I/6T (0.08 mil) (0.08 mil) 25% EMA 3% S&AB (0.08 mil) 10% PET-3(0.44 mil) (0.17 mil) 84 — 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-265% SEC 17% LLDPE (0.29 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 25% EMA3% S&AB (0.08 mil) 10% PET-3 (0.44 mil) (0.17 mil) 85 — 80% sscPE-3mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SBC-2 17% LLDPE (0.29 mil) 10%PA6I/6T (0.08 mil) (0.08 mil) 25% EMA 3% S&AB (0.08 mil) 10% PET-3 (0.44mil) (0.17 mil) 86 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65%SBC-2 17% LLDPE (0.29 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 25% EMA 3%S&AB (0.08 mil) 10% PET-3 (0.44 mil) (0.17 mil) 87 — 80% sscPE-3 mLLD-290% PA6/66 EVOH-2 mLLD-2 65% SBC-2 17% LLDPE (0.29 mil) 10% PA6I/6T(0.08 mil) (0.08 mil) 25% EMA 3% S&AB (0.08 mil) 10% PET-3 (0.44 mil)(0.17 mil) 88 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SBC-217% LLDPE (0.29 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 25% EMA 3% S&AB(0.08 mil) 10% PET-3 (0.44 mil) (0.17 mil) 89 W 80% sscPE-3 mLLD-2 90%PA6/66 EVOH-2 mLLD-2 65% SBC-2 17% LLDPE (0.29 mil) 10% PA6I/6T (0.08mil) (0.08 mil) 25% EMA 3% S&AB (0.08 mil) 10% PET-3 (0.44 mil) (0.17mil) 90 W 80% sscPE-3 mLLD-2 90% PA6/66 EVOH-2 mLLD-2 65% SBC-2 17%LLDPE (0.29 mil) 10% PA6I/6T (0.08 mil) (0.08 mil) 25% EMA 3% S&AB (0.08mil) 10% PET-3 (0.44 mil) (0.17 mil) 91 W 83.5% mLLD-2 90% PA 6 EVOH-490% PA 6 60% ssPE-3 (0.52 mil) 10% PA6I/6T (0.11 mil) 10% PA 6I/6Tg-LLDPE 15% LLDPE (0.44 mil) (0.44 mil) 30% g-SEC 5% S&AB 10% PET-3(0.55 mil) (0.41 mil) 92 W 83.5% mLLD-2 90% PA 6 EVOH-4 90% PA 6 60%ssPE-3 (0.52 mil) 10% PA6I/6T (0.11 mil) 10% PA 6I/6T g-LLDPE 15% LLDPE(0.44 mil) (0.44 mil) 30% g-SEC 5% S&AB 10% PET-3 (0.55 mil) (0.41 mil)93 C 83.5% mLLD-2 90% PA6/66 EVOH-4 90% PA 6/66 60% ssPE-3 (0.52 mil)10% PA6I/6T (0.11 mil) 10% PA 6I/6T g-LLDPE 15% LLDPE (0.44 mil) (0.44mil) 30% SEC 5% S&AB 10% PET-3 (0.55 mil) (0.41 mil) free shrink @185°F. (85 C.) Orient Front Vol (md & td) (% TD/% MD) Film % ° C._(t): tapeBack No. Layer 7 PET ° C._(b): bubble (% TD/MD %) Comment 1 PET-1 39.83.5X MD Front Severr corner delamination due to (0.63 mil) 3.3X TD 45/46differential shrink; tie layer unable to keep 73° C._(t) Back up; severecurl 93° C._(b) 40/42 2 PET-1 39.8 3.3X MD Front Edge and cornerdelamination; severe curl (0.63 mil) 3.1X TD 35/38 78° C._(t) Back 68°C._(b) 38/43 3 PET-1 30.3 3.5X MD Front Edge pucker and delamination;pre-shrunk (0.18 mil) 3.25X TD 32/40 sample curls 82° C._(t) Back 85°C._(b) 32/42 4 PET-1 30.3 3.5X MD DNR DNR (0.18 mil) 3.25X TD (DNR =data not recorded) 82° C._(t) 87° C._(b) 5 PET-1 30.3 3.5X MD DNR DNR(0.18 mil) 3.25X TD 88° C._(t) 83° C._(b) 6 PET-1 30.2 3.5X MD FrontSevere pucker and delamination all over (0.24 mil) 3.2X TD 30/41 edgeand corner can separate sample; 79° C._(t) Back severe curl 83° C._(b)36/40 7 PET-1 39.5 3.3X MD Front Corner and edge pucker anddelamination; (0.31 mil) 3.1X TD 38/40 severe curl 75° C._(t) Back 74°C._(b) 40/42 8 PET-1 30.2 3.3X MD Front Sample edge delaminates; (0.24mil) 3.1X TD 35/40 one sample is OK 76° C._(t) Back 74° C._(b) 35/43 9PET-1 39.9 3.3X MD Front Severe curl on pre-shrunk sample (0.63 mil)3.1X TD 35/40 77° C._(t) Back 73° C._(b) 37/48 10 PET-1 30.2 3.2X MDFront Severe edge delamination, pucker, (0.24 mil) 3.2X TD 40/47 sameplehas orange peel; severe 72° C._(t) Back curl 74° C._(b) 45/50 11 PET-130.2 3.2X MD Front DNR (0.24 mil) 3.5X TD 42/51 82° C._(t) Back 102°C._(b) 41/52 12 PET-1 39.8 3.5X MD Front Edge delamination; pre shrink(0.66 mil) 3.1X TD 55/62 sample has striations, non-uniform 78° C._(t)Back testure (possibly die lines); non- 56° C._(b) 54/55 optimizedsample 13 PET-1 41.8 3.5X MD Front No delamination, tie right adjacent(0.33 mil) 3.0X TD 30/40 to EVOH, sample has wrinkled 85° C._(t) Backappearance; very flat, not much 85° C._(b) 30/35 curl, sample as melt-ripples/orange peel 14 PET-1 41.8 3.5X MD Front No delamination butsample has (0.33 mil) —X TD 30/32 wrinkled appearance; right tie —°C._(t) Back layer adjacent to EVOH; very flat, —° C._(b) 30/45 not mcuhcurl, sample as melt- ripples/orange peel 15 PET-1 41.8 3.5X MD FrontMostly corner and some edge (0.33 mil) 3.1X TD 37/42 delamination; curlnot that bad 80° C._(t) Back 71° C._(b) 32/37 PRO PET-1 41.8 3.5X MD DNRDNR 16 (0.33 mil) 3.1X TD 76° C._(t) 82° C._(b) 17 PET-1 41.8 3.4X MDDNR DNR (0.33 mil) 3.1X TD 80° C._(t) 99° C._(b) 18 PET-1 30.2 3.0X MDFront corner delamination; curl prevents (0.24 mil) 3.4X TD 38/38 grossdelamination, run with 80° C._(t) Back sealant out; very severe curl100° C._(b) 37/33 19 PET-1 15.1 3.2X MD Front corner delamination; curlprevents (0.24 mil) 3.8X TD 38/38 gross delamination; severely 80°C._(t) Back wrinkled film; not optimized, may 96° C._(b) 37/33 be due toprocess conditions; run with 0 kGy irradiation 20 PET-1 15.1 3.2X MDFront Edge and corner delamination; (0.24 mil) 3.8X TD 40/42 severelywrinkled film; not 80° C._(t) Back optimized, may be due to process 96°C._(b) 44/47 conditions; run with 31 kGy irradiation 21 PET-1 15.1 3.2XMD Front Severe edge and (0.24 mil) 3.8X TD 47/52 corner delamination;severely 80° C._(t) Back wrinkled film; not optimized, may 96° C._(b)44/49 be due to process conditions; run with 61 kGy irradiation 22 PET-124.7 3.5X MD L + T DNR (0.39 mil) 3.1X TD 73% 85° C._(t) 85° C._(b) 23PET-1 24.7 3.2X MD Front DNR (0.39 mil) 3.5X TD 33/40 80° C._(t) Back103° C._(b) 29/40 24 PET-1 24.7 3.2X MD Front No delamination; severecurl (0.39 mil) 3.4X TD 33/41 80° C._(t) Back 104° C._(b) 36/45 25 85%sscPE-3 29.7 3.1X MD Front No delamination 15% LLDPE 3.6X TD 76% (L + T)(0.71 mil) 78° C._(t) Back 100° C._(b) 80% (L + T) 26 85% sscPE-3 29.73.2X MD Front No delamination 15% LLDPE 3.6X TD 81% (L + T) (0.71 mil)76° C._(t) Back 97° C._(b) 85% (L + T) 27 85% sscPE-3 29.7 3.2X MD FrontNo delamination 15% LLDPE 3.5X TD 76% (L + T) (0.71 mil) 78° C._(t) Back97° C._(b) 81% (L + T) 28 85% sscPE-3 29.7 3.2X MD Front No delamination15% LLDPE 3.7X TD 73% (L + T) (0.71 mil) 76° C._(t) Back 94° C._(b) 76%(L + T) 29 85% sscPE-3 29.7 3.1X MD Front No delamination; uneventexture ~15% LLDPE 3.7X TD 30/37 of sample; white lines (0.71 mil) 79°C._(t) Back 97° C._(b) 27/35 30 85% sscPE-3 29.7 3.1X MD Front Some edgepucker but no 15% LLDPE 3.7X TD 40/44 delamination; sample (0.71 mil)80° C._(t) Back rigid, uneven; sample has some 97° C._(b) 43/47 curl 3185% sscPE-3 31.8 3.2X MD Front No delamination; sample has some 15%LLDPE 3.7X TD 42/42 curl (0.71 mil) 76° C._(t) Back 91° C._(b) 42/44 3285% sscPE-3 31.8 3.2X MD Front Curled up a lot 15% LLDPE 3.7X TD 75%(L + T) (0.63 mil) 79° C._(t) Back 93° C._(b) 90% (L + T) 33 PET-1 29.73.2X MD Front No delamination; shrunk sample (0.47 mil) 3.7X TD 40/44clearer than un shrunk; sample 86° C._(t) Back striated, not uniforminin 100° C._(b) 39/42 appearance; sample has some curl 34 PET-1 29.7 3.3XMD Front DNR (0.47 mil) 3.8X TD 74% (L + T) 77° C._(t) Back 96° C._(b)69% (L + T) 35 PET-1 29.7 3.2X MD Front DNR (0.47 mil) 4.0X TD 34/40 81°C._(t) Back 97° C._(b) 30/40 36 PET-1 29.7 3.1X MD Front DNR (0.47 mil)3.9X TD 76% (L + T) 82° C._(t) Back 99° C._(b) 74% (L + T) 37 PET-1 29.73.1X MD Front DNR (0.47 mil) 3.9X TD 34/40 79° C._(t) Back 97° C._(b)30/40 38 PET-1 29.7 3.3X MD Front DNR (0.47 mil) 3.5X TD 38/41 78°C._(t) Back 82° C._(b) 32/38 39 PET-1 29.7 3.2X MD Front 70μ filmthickness; (0.47 mil) 3.9X TD 36/44 DNR 81° C._(t) Back 94° C._(b) 30/3940 PET-1 29.7 3.1X MD Front 40μ film thickness; (0.47 mil) 3.9X TD 31/40DNR 80° C._(t) Back 99° C._(b) 32/40 41 PET-1 29.7 3.4X MD Front Has alittle curl (0.47 mil) 3.4X TD 68% (L + T) 77° C._(t) Back 86° C._(b)74% (L + T) 42 PET-1 29.7 3.4X MD Front 40μ film thickness; (0.47 mil)2.2X TD 39/45 DNR 75° C._(t) Back 91° C._(b) 37/47 43 PET-1 29.7 3.4X MDFront No delamination; sample is (0.47 mil) 3.5X TD 33/402 wrinkled,rigid and uneven; severe 76° C._(t) Back curl; curls up into roll 86°C._(b) DNR- 44 PET-1 29.7 3.2X MD Front No delamination; sample is (0.47mil) 3.9X TD 40/482 wrinkled, rigid and uneven; severe 89° C._(t) Backcurl; curls up into roll 95° C._(b) 38/46 45 PET-1 29.7 3.2X MD Front Nodelamination; (0.47 mil) 3.9X TD 38/42 some curl, not bad 80° C._(t)Back 97° C._(b) 38/42 46 PET-1 29.7 3.2X MD Front DNR (0.47 mil) 3.9X TD71% (L + T) 83° C._(t) Back 95° C._(b) 73% (L + T) 47 PETG 29.7 3.5X MDFront Difficult to obtain stable bubble; (0.47 mil) 3.8X TD 71% (L + T)material weak 89° C._(t) Back DNR° C._(b) 76% (L + T) 48 PET-1 35.2 3.2XMD DNR DNR (0.28 mil) 3.2X TD 85° C._(t) 93° C._(b) 49 PET-1 29.7 3.3XMD Front No delamination; sample had (0.47 mil) 3.6X TD 35/40 severecurl 77° C._(t) Back 88° C._(b) 34/42 50 PET-1 29.7 3.4X MD Front Nodelamination; some curl (0.47 mil) 3.6X TD 37/46 76° C._(t) Back 87°C._(b) 39/46 51 PETG 29.9 3.7X MD No Sample No sample; poor bubblestability (0.47 mil) 3.5X TD Obained due to PETG 80° C._(t) 101° C._(b)52 PET-1 30.1 3.3X MD Front DNR (0.24 mil) 3.5X TD 30/40 81° C._(t) Back88° C._(b) 34/43 53 PET-1 46 3.2X MD Front 70μ film; no delamination;one (0.83 mil) 3.9X TD 38/41 corner has pucker in one sample, 84° C._(t)Back flat, not much curl 97° C._(b) 39/41 54 PET-1 46 3.2X MD Front 40μfilm thickness; (0.83 mil) 4.1X TD 35/37 DNR 82° C._(t) Back 97° C._(b)33/37 55 PET-2 40 3.4X MD Front Sample hard and brittle; severe (0.63mil) 4.1X TD 47/52 curl 93° C._(t) Back 98° C._(b) 50/53 56 PET-2 273.3X MD Front 40μ film thickness; (0.43 mil) 4.01X TD 40/45 Nodelamination; 91° C._(t) Back severe curl 94° C._(b) 40/44 57 PET-1 303.3X MD Front 70μ film thickness; (0.47 mil) 3.6X TD 38/46 DNR 79°C._(t) Back 85° C._(b) 36/40 58 PET-1 30 3.3X MD Front 40μ filmthickness; no (0.47 mil) 3.6X TD 35/35 delamination; Corner pucker; 82°C._(t) Back wrinkled samples, not much curl 86° C._(b) 31/40 59 PET-1 303.3X MD Front 70μ film thickness; (0.47 mil) 3.6X TD 40/45 DNR 81°C._(t) Back 86° C._(b) 37/40 60 PET-1 30 3.2X MD Front 40μ filmthickness; (0.47 mil) 3.6X TD 40/45 One sample had edge 77° C._(t) Backdelamination; sample curls 81° C._(b) 41/45 61 PET-1 30 3.2 X MD Front40μ film thickness; (0.47 mil) 3.6 X TD 37/44 No delamination; 77°C._(t) Back Sample curls 81° C._(b) 35/45 62 PET-1 30 DNR Front 40μ filmthickness; hand sample (0.47 mil) 36/42 only; could not stabilize fordata; Back sample curls 37/42 63 PET-1 3.2 X MD Front No delamination(0.47 mil) 3.6 X TD DNR 73° C._(t) Back 91° C._(b) DNR 64 PET-1 30 3.0 XMD Front 70μ film thickness; stable process; (0.77 mil) 3.9 X TD 29/33did not delaminate 81° C._(t) Back 93° C._(b) 29/37 65 PET-1 30 3.3X MDFront better tie; no stage 2 (0.47 mil) 3.7X TD 35/40 delamination;stable process; 77° C._(t) Back sample does curl but manageable; 88°C._(b) 34/42 stage 1 delamination on use in flow wrap process 66 PET-130 DNR DNR No sample obtained; (0.83 mil) stage 4 delamination, i.e., attape edge 67 PET-1 30 DNR DNR DNR for free shrink delamination; (0.47mil) stage 1 delamination on use in flow wrap process 68 PET-1 30 3.1XMD Front 70μ film thickness; (0.83 mil) 3.8X TD 28/36 process relativelystable; 83° C._(t) Back no delamination upon free shrink; 93° C._(b)34/43 but stage 1 delamination on use in flow wrap process 69 PET-1 293.0X MD Front 70μ film thickness; (0.77 mil) 3.9X TD 29/33 very stableprocess; no 81° C._(t) Back delamination 93° C._(b) 29/37 70 PET-1 30DNR DNR unstable process; (0.83 mil) could not make film 71 PET-1 303.0X MD Front 70μ film thickness; unstable (0.83 mil) 3.9X TD 28/35process; could not make film 80° C._(t) Back 92° C._(b) 29/36 72 95%PET-1 28 3.2X MD Front 40μ film thickness; 5% EMA 3.7X TD 34/41 stableprocess; no delamination (0.47 mil) 80° C._(t) Back 90° C._(b) 34/40 73PET-1 28 3.1X MD Front 70μ film thickness; film (0.78 mil) 3.8X TD 34/41delaminated upon shrink 83° C._(t) Back 93° C._(b) 28/35 74 PET-1 283.0X MD Total free Delaminated upon shrinking (0.78 mil) 3.9X TD shrinkabout 83° C._(t) 70% 95° C._(b) 75 PET-1 28 3.1X MD Front 70μ filmthickness; stable process; (0.78 mil) 3.8X TD 30/37 no delamination 83°C._(t) Back 92° C._(b) 29/37 76 PET-1 28 3.1X MD Front 70μ filmthickness; stable process; (0.78 mil) 3.8X TD 30/39 no delamination 83°C._(t) Back 93° C._(b) 30/38 77 PET-1 28 3.1X MD Front 70μ filmthickness; some ripples; (0.78 mil) 3.8X TD 31/36 stable process; nodelamination 82° C._(t) Back 92° C._(b) 32/40 78 PET-1 28 3.1X MD DNR70μ film thickness; (0.78 mil) 3.8X TD stable process; no delamination81° C._(t) 92° C._(b) 79 PET-1 28 3.1X MD Front 70μ film thickness;(0.77 mil) 3.8X TD 29/38 no delaminatiom 83° C._(t) Back 10% polyamide93° C._(b) 28/37 stable process 80 PET-1 24 3.1X MD Front 70μ filmthickness; 15% (0.63 mil) 3.8X TD 24/33 polyamide 76° C._(t) Back stableprocess; 89° C._(b) 24/33 no delamination 81 95% PET-1 28 3.2X MD Front40μ film thickness; 5% EMA 3.7X TD 36/36 Stable process; hazy film (0.47mil) DNR ° C._(t) Back No data on delamination DNR ° C._(b) 31/37 82 95%PET-1 28 3.2X MD Front 40μ film thickness; 5% EMA-2 3.7X TD 32/34Enhanced tie similar to Example (0.44 mil) 74° C._(t) Back 67; needthicker tie layer to 82° C._(b) 31/35 prevent melt ripples; nodelamination 83 95% PET-1 27 3.2X MD DNR 40μ film thickness; 5% EBA 3.7XTD Stable process; (0.44 mil) 74° C._(t) no delamination 82° C._(b) 8490% PET-1 25 DNR DNR Severe melt ripples; 6.5% SEC could not run 2.5%EMA 1% PET-3 (0.44 mil) 85 95% PET-1 25 DNR DNR 40μ film thickness; 5%SBC-2 unstable; melt ripples; could not (0.44 mil) produce film 86 PET-129 3.2X MD Front 40μ film thickness; (0.44 mil) 3.7X TD 31/33 nodelamination 74° C._(t) Back 84° C._(b) 32/36 87 97% PET-1 27 DNR DNR40μ film thickness; gritty tape, 3% EMA-3 surges, did not make 90/10,(0.44 mil) agglomeration of pellets in blender mixer, no samples; 97/3could be made, gritty films 88 95% PET-1 28 3.1X MD Front 40μ filmthickness; 5% EVA-2 3.8X TD 33/36 (0.44 mil) 74° C._(t) Back 82° C._(b)31/34 89 95% PET-1 28 3.2X MD Front 40μ film thickness; 4% EMA-4 3.8X TD35/39 1% Et-Cop 74° C._(t) Back (0.44 mil) 83° C._(b) 32/34 90 95% PET-128 3.1X MD DNA 40μ film thickness 4% EMA 3.8X TD 1% EMA-3 74° C._(t)(0.44 mil) 83° C._(b) 91 PET-1 10 DNA 27% MD No Delamination (0.28 mil)35% TD 92 PET-1 10 DNA 26% MD No Delamination (0.28 mil) 32% TD 93 PET-110 DNA 27% MD Delamination (0.28 mil) 34% TD “—”: film had tie layercomprising styrene based polymer but reason for inoperability believedunrelated to tie layer composition.

Films 1-90 are directed to films having an outer polyester layer, abarrier layer, and at least one tie layer between the outer polyesterlayer and the barrier, without a polyamide layer between the outerpolyester layer and the barrier layer. A review of these films revealsthe effect of having a styrene-based polymer in the tie layer betweenthe outer polyester layer and the barrier layer: of the nineteen filmslacking a styrene-based polymer in this tie layer, recorded dataindicating the presence of delamination is set forth for eleven of thesefilms (i.e., films 1, 2, 3, 6, 7, 8, 10, 12, 15, 18, and 74). Thisdelamination was delamination upon conducting unrestrained free shrinkvia immersion in 85° C. water for 8 seconds, using ASTM D2732 (stage 2delamination), or delamination upon handling the film after orientationand annealing (stage 3 delamination) or delamination upon extrusion ofthe tape, i.e., before orientation (stage 4 delamination). No indicationof whether or not delamination occurred was recorded for the eightremaining films (i.e., films 4, 5, 9, 11, 16, 17, 52 and 72) whichlacked a tie layer containing a styrene-based polymer. Each of theeighteen films lacking a styrene-based polymer in the tie layer isdesignated as a comparative example (“C”) in the second column of Table2.

In contrast, in each of the remaining eighty-one films in Table 2, thetie layer between the outer polyester layer and the barrier layercontained a styrene-based polymer. Thirty-four of the eighty-one films(i.e., films 13, 14, 24-31, 33, 43-45, 49, 50, 56, 58, 60, 61, 63, 64,65, 69, 72, 75-80, 82, 83, and 86) included an express commentindicating that these films exhibited no delamination. Twenty-five ofthe eighty-one films (i.e., films 22, 23, 32, 34-42, 46-48, 53-55, 57,59, 62, 81, and 88-90) included no express comment on the presence orabsence of delamination. However, if stage 2, 3, or 4 delamination hadoccurred for any of these films, it is believed that data would havebeen recorded of such delamination if in fact it had occurred, as thecomment “delaminated” was recorded for various samples outside thisgroup. As no such comment was recorded, it is believed that thesetwenty-five samples also did not experience stage 2, 3, or 4delamination.

Six of the eighty-one films (i.e., films 51, 70, 71, 84, 85, and 87)could not be produced for various reasons such as unstable process andsurges. Another six films (i.e., films 19, 20, 21, 66, 67, and 68)exhibited delamination even though they had a styrene-based polymer inthe tie layer adjacent the outer polyester layer. For three of thesefilms, i.e., films 19, 20, and 21, data indicates the potential reasonfor the delamination is that the process conditions were not optimized.The remaining three films that delaminated, i.e., films 66, 67, and 68,it is not known why delamination occurred.

In summary, it was found that of the ninety heat shrinkable films, thetotality of the data supports the conclusion that presence of a tielayer containing a styrene-based copolymer between the PET layer and thebarrier layer decreased or eliminated stage 2 through stage 4 filmdelamination. In contrast, it was discovered that heat shrinkable filmswhich lacked a styrene based copolymer between the PET layer and thebarrier layer had a substantially greater chance of exhibiting stage 2to stage 4 delamination.

Fourteen films (i.e., films 64, 69, 70, 79, 80, and 82-90) had a tielayer containing a blend of the styrene-based polymer with a copolyesterhaving a low melting point (121° C.). Some of these films were used tomake packaging articles that exhibited superior burst strength due totheir enhanced resistance to delamination.

The films that delaminated upon shrinking exhibited visible signs ofdelamination. These visible signs of delamination included, among othervisible signs, one or more of (i) delaminated layers at the sample edge(ii) “white spots” inward of the sample edge, caused by layerdelamination, (iii) a highly wrinkled film appearance in discrete areasor throughout the sample, sometimes on only one principal surface of thesample, and (iv) areas of decreased film transparency, or whole-filmdecrease in transparency.

Films 91-93 are directed to multilayer heat shrinkable coextruded filmshaving an outer polyester layer, a first inner layer comprising apolyamide, and a second inner layer between the polyester layer and thelayer comprising the polyamide. Film 91 and Film 92 above were workingexamples in accordance with the present invention. Film 91 and Film 92each had an outer layer comprising a polyethylene terephthalatecopolymer having a melt point of 255° C., and a first inner polyamidelayer made up of a blend of 90 wt % semicrystalline polyamide (PA6) and10 wt % amorphous polyamide (PA 6I/6T). Between the outer polyesterlayer and the polyamide layer was a tie layer comprising a blend of (i)60 wt % anhydride-grafted LLDPE, 30 wt % anhydride-grafted styreneethylene butylene triblock copolymer, and 10 wt % polyester.

During production, both Film 91 and Film 92 were produced as film tubingwithout significant process instability, i.e., without melt ripples andwithout bubble breaks. Moreover, after production, the heat-shrinkablefilm tubings of Film 91 and Film 92 were each slit and wound up as flatfilm rollstock. Samples of each of Film 91 and Film 92 were shrunk in ahot water bath by immersion in water at 85° C. for 8 seconds. NeitherFilm 91 nor Film 92 experienced delamination during production or duringshrinking.

The rollstock was thereafter used on a horizontal form fill and sealmachine as illustrated in FIG. 16, described above. After sealing acrossthe tubing upstream of the meat product, the resulting open package(318) having the meat therein was forwarded to a vacuum chamber machine.While in the vacuum chamber, atmosphere was evacuated from inside thepackage and the package was sealed closed. The excess film was then cutoff above the heat seal and the resulting packaged product was sentthrough a hot water bath to shrink the film tight around the meatproduct. Neither Film 91 nor Film 92 experienced delamination duringproduction or during shrinking.

Film 93 was a comparative example. Film 93 was a heat-shrinkable filmproduced in the same manner as used for the production of Film 91 andFilm 92. Film 93 differed from Film 91 only in that the tie layerbetween the outer polyester layer and the inner polyamide layercomprised a blend of 60 wt % anhydride grafted LLDPE, 30 wt %non-grafted styrene-ethylene-butylane copolymer, and 10 wt % polyester.That is, the 3-component blend in the tie layer of Film 93 used 30 wt %non-grafted terpolymer rather than the 30 wt % anhydride-graftedstyrene-ethylene-butylene copolymer used in Film 91 and Film 92.

Unlike Film 91, during production Film 93 exhibited process instabilityin the formation of melt ripples. Moreover, after production, Film 93delaminated upon immersion for 8 seconds in water at 85° C.

Although the present invention has been described with reference to thepreferred embodiments, it is to be understood that modifications andvariations of the invention exist without departing from the principlesand scope of the invention, as those skilled in the art will readilyunderstand. Accordingly, such modifications are in accordance with theclaims set forth below.

What is claimed is:
 1. A multilayer heat-shrinkable film comprising: (A)a first layer comprising a first polyester, the first layer being anouter layer; (B) a second layer which serves as an O₂-barrier layer, thesecond layer comprising at least one member selected from the groupconsisting of saponified ethylene/vinyl acetate copolymer, polyamideMXD6, polyamide 6I/6T, polyamide 6, polyvinylidene chloride,polyethylene naphthalate, polytrimethylene terephthalate, liquid crystalpolymer, and O₂-scavenger; (C) a third layer between the first layer andthe second layer, the third layer serving as a tie layer, the thirdlayer comprising a blend of a first blend component comprising astyrene-based copolymer and a second blend component comprising a cyclicolefin copolymer, the styrene-based polymer making up from 10 to 90 wt %of the weight of the third layer, the styrene-based polymer comprisingat least one member selected from the group consisting ofstyrene-ethylene-butylene-styrene copolymer, styrene-butadiene-styrenecopolymer, styrene-isoprene-styrene copolymer,styrene-ethylene-butadiene-styrene copolymer,styrene-(ethylene-propylene rubber)-styrene copolymer, andpolystyrene-poly(ethylene-propylene)-polystyrene copolymer; and whereinthe multilayer heat shrinkable film is in the form of a seamless tubinghaving a lay-flat width of from 40 to 1000 millimeters, a thickness offrom 1 to 5 mils, and a total free shrink at 85° C. of from 40% to 90%measured in accordance with a modified free shrink test otherwise inaccordance with ASTM D 2732, and the polyester is present in the film inan amount of at least 2 vol %, based on total film volume.
 2. Themultilayer heat shrinkable film according to claim 1, wherein the blendfurther comprises a third blend component which comprises at least onemember selected from the group consisting of second polyester and amodified polyolefin.
 3. The multilayer heat shrinkable film according toclaim 2, wherein the styrene-based copolymer of the first blendcomponent comprises at least one member selected from the groupconsisting of styrene-ethylene-butylene-styrene block copolymer andstyrene-butadiene block copolymer; the second blend component furthercomprises an ethylene/acrylate copolymer; the second polyester of thethird blend component comprises a copolyester; and the modifiedpolyolefin of the third blend component comprises an anhydride-modifiedpolyolefin.
 4. The multilayer heat shrinkable film according to claim 3,wherein: (i) the first blend component is present in an amount from 10to 90 wt %, based on total blend weight, thestyrene-ethylene-butylene-styrene block copolymer is astyrene-ethylene-butylene-styrene triblock copolymer, thestyrene-butadiene block copolymer is a styrene-butadiene multiblockcopolymer; (ii) the ethylene/acrylate copolymer of the second blendcomponent is an ethylene/methyl acrylate copolymer and is present in anamount of from 10 to 90 wt %, based on total blend weight; and (iii) thethird blend component is present in an amount of from 5 to 30 wt %,based on total blend weight, the copolyester of the third blendcomponent is an amorphous copolyester, having a melting point of from100° C. to 185° C., and the anhydride-modified polyolefin of the thirdblend component is an anhydride-modified ethylene/alpha-olefincopolymer.
 5. The multilayer heat shrinkable film according to claim 3,wherein the third blend component is present in an amount from 5 to 15wt %, based on total blend weight, the copolyester of the third blendcomponent having a melting point of from 105° C. to 140° C., and theanhydride-modified polyolefin of the third blend component is ananhydride-modified linear low density polyethylene.
 6. The multilayerheat shrinkable film according to claim 1, wherein the second layercomprises saponified ethylene vinyl acetate copolymer.
 7. The multilayerheat shrinkable film according to claim 1, wherein the first polyestercomprises at least one semi-crystalline polyester selected from thegroup consisting of polyethylene terephthalate homopolymer, polyethyleneterephthalate copolymer, polybutylene terephthalate homopolymer,polybutylene terephthalate copolymer, polynaphthalene terephthalatehomopolymer, polynaphthalene terephthalate copolymer, polyethylenefuranoate homopolymer, and polyethylene furanoate copolymer, wherein thesemicrystalline polyester has a melting point of from 80° C. to 265° C.8. The multilayer heat shrinkable film according to claim 1, wherein thefirst polyester comprises amorphous polyester.
 9. The multilayer heatshrinkable film according to claim 1, wherein the film exhibits a totalfree shrink at 85° C. of at least 30% measured in accordance with themodified free shrink test otherwise in accordance with ASTM D 2732, andthe first polyester is present in the film in an amount of at least 15vol %, based on total film volume.
 10. The multilayer heat shrinkablefilm according to claim 1, wherein the film exhibits a total free shrinkat 85° C. of from 40% to 90% measured in accordance with the modifiedfree shrink test otherwise in accordance with ASTM D 2732, and the firstpolyester is present in the film in an amount of at least 20 vol %,based on total film volume.
 11. The multilayer heat shrinkable filmaccording to claim 1, wherein the third layer is a first tie layer andthe multilayer, heat-shrinkable film further comprises: a fourth layerwhich is a second outer layer and which serves as a heat seal layer andwhich comprises at least one member selected from the group consistingof polyolefin, polyamide, polyester, polyvinyl chloride, and ionomerresin; a fifth layer which is between the fourth layer and the secondlayer, the fifth layer serving as a second tie layer, the fifth layercomprising at least one member selected from the group consisting ofmodified polyolefin, modified ethylene/unsaturated acid copolymer,modified ethylene/unsaturated ester copolymer, and polyurethane; and asixth layer which is between the second layer and the fifth layer, thesixth layer comprising at least one member selected from the groupconsisting of (i) an amorphous polyamide, (ii) a blend of asemicrystalline polyamide and amorphous polyamide, and (iii) a blend ofpolyamide 6/12 and a different semi-crystalline polyamide.
 12. Themultilayer heat shrinkable film according to claim 11, furthercomprising a supplemental tie layer between the second layer and thethird layer, with the supplemental tie layer comprising at least onemember selected from the group consisting of modified polyolefin,modified ethylene/unsaturated acid copolymer, modifiedethylene/unsaturated ester copolymer, and polyurethane.
 13. Themultilayer heat shrinkable film according to claim 1, wherein the secondlayer comprises saponified ethylene/vinyl acetate copolymer and thethird layer comprises a blend of: (i) the styrene-based polymer, (ii) amodified polyolefin, and (iii) a second polyester.
 14. The multilayerheat shrinkable film according to claim 1, wherein the film is in theform of a seamless tubing having a lay-flat width of from 300 to 1000millimeters, a thickness of from 2 to 5 mils, and a total free shrink at85° C. of from 40% to 90% measured in accordance with a modified freeshrink test otherwise in accordance with ASTM D
 2732. 15. A multilayerheat-shrinkable film comprising: (A) a first outer layer comprising afirst polyester; (B) a second outer layer which serves as a heat seallayer; (C) a first inner layer comprising a polyamide; (D) a secondinner layer between the first inner layer and the first outer layer, thesecond inner layer serving as a tie layer, the second inner layercomprising a blend of: (i) a first blend component comprising ananhydride-functional ethylene/alpha-olefin polyolefin; (ii) a secondblend component comprising an anhydride-functional styrene/butadieneblock copolymer, and (iii) a third blend component comprising asemi-crystalline, thermoplastic, linear saturated polyester resin havinga density of from 1.15 to 1.30 g/cm³, a melting point of from 150° C. to160° C., and a melt index of from 0.5 to 2 g/10 min; and wherein themultilayer heat-shrinkable film exhibits a total free shrink at 85° C.of at least 10 percent measured in accordance with a modified freeshrink test otherwise in accordance with ASTM D 2732, and the firstpolyester is present in the film in an amount of at least 5 volume %,based on total film volume.
 16. The multilayer heat-shrinkable filmaccording to claim 15, wherein: the first blend component comprises ananhydride-functional ethylene/alpha-olefin copolymer, and the secondblend component comprises at least one anhydride-functionalstyrene/butadiene block copolymer selected from the group consisting ofstyrene/maleic anhydride copolymer, anhydride-functionalstyrene-ethylene-butylene-styrene copolymer, anhydride-functionalstyrene-butadiene-styrene copolymer, anhydride functionalstyrene-isoprene-styrene copolymer, anhydride-functionalstyrene-ethylene-butadiene-styrene copolymer, and anhydride-functionalgrafted styrene-(ethylene-propylene rubber)-styrene copolymer.
 17. Themultilayer heat-shrinkable film according to claim 15, wherein: thefirst polyester comprises polyethylene terephthalate having a meltingpoint of at least 240° C.; and the polyamide in the first inner layercomprises at least one member selected from the group consisting of: (a)a blend of a semi-crystalline polyamide and an amorphous polyamide; (b)a blend of a semi-crystalline polyamide and polyamide 6/12; and (c) 100%amorphous polyamide.
 18. The multilayer heat-shrinkable film accordingto claim 15, wherein the second outer layer which serves as the heatseal layer comprises at least one member selected from the groupconsisting of polyolefin, polyamide 6/12, polyamide 12, ionomer resin,ethylene/unsaturated acid copolymer, ethylene/unsaturated estercopolymer, polyester having melting point of up to 150° C.
 19. Themultilayer heat-shrinkable film according to claim 18, wherein thesecond outer layer comprises a homogeneous ethylene/alpha-olefincopolymer having a density of from 0.89 to 0.91 g/cm³.
 20. Themultilayer heat-shrinkable film according to claim 15, wherein the firstouter layer makes up from 5 to 20 volume % based on total film volume,the second outer layer makes up from 15 to 40 volume % based on totalfilm volume, the first inner layer makes up from 10 to 30 volume % basedon total film volume, and the second inner layer makes up from 10 to 30volume % based on total film volume.
 21. The multilayer heat-shrinkablefilm according to claim 15, wherein the film has a total thickness offrom 1.5 mils to 4 mils.
 22. The multilayer heat-shrinkable filmaccording to claim 15, wherein the first blend component makes up from30 to 80 wt % based on total layer weight, the second blend componentmakes up from 10 to 50 wt % based on total layer weight, and the thirdblend component makes up from 2 to 20 wt % based on total layer weight.23. The multilayer heat-shrinkable film according to claim 15, whereinthe second inner layer is directly adhered to both the first outer layerand the first inner layer.
 24. The multilayer heat-shrinkable filmaccording to claim 15, wherein the film exhibits a total free shrink at85° C. of at least 40 percent measured in accordance with a modifiedfree shrink test otherwise in accordance with ASTM D
 2732. 25. Themultilayer heat-shrinkable film according to claim 15, wherein thesecond outer layer which serves as the heat seal layer comprises atleast one member selected from the group consisting of polyolefin,polyamide 6/12, polyamide 12, ionomer resin, ethylene/unsaturated acidcopolymer, ethylene/unsaturated ester copolymer, polyester havingmelting point of up to 150° C.
 26. The multilayer heat-shrinkable filmaccording to claim 25, wherein the second outer layer comprises ahomogeneous ethylene/alpha-olefin copolymer having a density of from0.89 to 0.91 g/cm³.
 27. A multilayer heat-shrinkable film comprising:(A) a first outer layer comprising a first polyester; (B) a second outerlayer which serves as a heat seal layer, the second outer layercomprising a blend of from 75 to 90 wt % homogeneousethylene/alpha-olefin copolymer having a density of from 0.895 to 0.905g/cm³, and from 10 to 25 wt % of a heterogeneous ethylene/alpha-olefincopolymer having a density of from 0.915 to 0.925 g/cm³; (C) a firstinner layer comprising a blend of (i) from 60 to 95 wt % of at least onemember selected from the group consisting of polyamide 6 and polyamide6/66, and (ii) from 5 to 40 wt % of polyamide 6I/6T; (D) a second innerlayer between the first inner layer and the first outer layer, thesecond inner layer serving as a tie layer, the second inner layercomprising a blend of (i) from 50 to 70 wt % of an anhydride-functionalethylene/alpha-olefin copolymer, (ii) from 20 to 40 wt %anhydride-functional styrene/butadiene block copolymer; and (iii) from 5to 15 wt % of a second polyester; (E) a third inner layer which servesas an O₂-barrier layer, the third inner layer comprising at least onemember selected from the group consisting of saponified ethylene/vinylacetate copolymer, polyamide MXD6, polyamide 6I/6T, polyamide 6,polyvinylidene chloride, polyethylene naphthalate, polytrimethyleneterephthalate, liquid crystal polymer, and O₂-scavenger, the third innerlayer being between the first inner layer and the second outer layer;(F) a fourth inner layer which serves as a tie layer, the fourth innerlayer being between the second outer layer and the third inner layer;(G) a fifth inner layer between the third inner layer and the fourthinner layer, the fifth inner layer comprising a blend of (i) from 60 to95 wt % of at least one member selected from the group consisting ofpolyamide 6 and polyamide 6/66, and (ii) from 5 to 40 wt % of polyamide6I/6T.
 28. The multilayer heat-shrinkable film according to claim 27,wherein: (A) the polyester in the first outer layer comprisespolyethylene terephthalate copolymer in an amount of at least 95 wt %,based on total layer weight; (E) the third inner layer comprisessaponified ethylene vinyl acetate copolymer; (F) the fourth inner layercomprises an anhydride-grafted ethylene/alpha-olefin copolymer.
 29. Themultilayer heat-shrinkable film according to claim 27, wherein the firstouter layer makes up from 5 to 15 volume % based on total film volume,the second outer layer makes up from 15 to 25 volume % based on totalfilm volume, the first inner layer makes up from 10 to 20 volume % basedon total film volume, the second inner layer makes up from 10 to 20volume % based on total film volume, the third inner layer makes up from2 to 10 volume % based on total film volume, the fourth inner layermakes up from 20 to 30 volume % based on total film volume, and thefifth inner layer makes up from 10 to 20 volume % based on total filmvolume.
 30. The multilayer heat-shrinkable film according to claim 27,wherein the polyester in the first outer layer comprises polyethyleneterephthalate copolymer in an amount of at least 95 wt %, based on totallayer weight, the third inner layer comprises saponified ethylene vinylacetate copolymer, and the fourth inner layer comprises ananhydride-grafted ethylene/alpha-olefin copolymer.
 31. The multilayerheat-shrinkable film according to claim 30, wherein the first outerlayer makes up from 5 to 15 volume % based on total film volume, thesecond outer layer makes up from 15 to 25 volume % based on total filmvolume, the first inner layer makes up from 10 to 20 volume % based ontotal film volume, the second inner layer makes up from 10 to 20 volume% based on total film volume, the third inner layer makes up from 2 to10 volume % based on total film volume, the fourth inner layer makes upfrom 20 to 30 volume % based on total film volume, and the fifth innerlayer makes up from 10 to 20 volume % based on total film volume.